ABS POLYLAC® PA-709 TAIWAN CHIMEI
57
- Properties:High impact resistanceLow temperature resistanc
- Usages:Automotive sector
- Certificates:MSDSRoHSULTDSTDSULMSDSRoHSSVHCProcessingStatementREACH
Compare
View PricesTechnical Data Sheet
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| notes | 在射出周期中勿将热融胶长期停留在加热管中 | ||
| 超高耐冲击强度押管用。 | |||
| purpose | 水管配件 / 汽车前后扰流板 / 摩托车挡板 / 押出水管 / 安全帽 |
| processability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dry conditions | 80°C下烘料约2~3小时 | ||
| process temperature | 180~220 °C | ||
| 190~230 °C | |||
| 180~230°C °C | |||
| screw speed | - rpm | ||
| Temperature | 30-70 °C | ||
| Melt Temperature | - °C | ||
| pressure | - Mpa |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Izod notch impact strength | ASTM D256/ISO 179 | 37（6.9） kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | - % | |
| Tensile modulus | ASTM D638/ISO 527 | - kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 400（5，670） kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 40 % | |
| Rockwell hardness | ASTM D785 | R-102 | |
| Flexural modulus | ASTM D790/ISO 178 | 23000（32000） kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 640（9，070） kg/cm²(MPa)[Lb/in²] | |
| Charpy impact strength | ASTM D256/ISO 179 | - kg·cm/cm(J/M)ft·lb/in | |
| Izod notch impact strength | ASTM D256/ISO 179 | - kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 45（8.4） kg·cm/cm(J/M)ft·lb/in | ||
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | - % |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.03 | |
| Mold Shrinkage | ASTM D955 | - % | |
| Water absorption rate | ASTM D570/ISO 62 | - % | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 0.5 g/10min | |
| ASTM D1238/ISO 1133 | 5 g/10min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Combustibility (rate) | UL94 | 1.6mmHB | |
| ASTM D648/ISO 75 | 99（210） ℃（℉） | ||
| ASTM D648/ISO 75 | 88（190） ℃（℉） | ||
| vicat | ASTM D1525/ISO R306 | 105（221） ℃（℉） | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | - mm/mm.℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.