Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS PA-709 TAIWAN CHIMEI
POLYLAC®
Automotive sector
High impact resistance、Low temperature resistanc
MSDS
RoHS
UL
TDS
TDS
UL
MSDS
RoHS
SVHC
Processing
Statement
REACH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | TAIWAN CHIMEI/PA-709 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 640（9，070） kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 23000（32000） kg/cm²(MPa)[Lb/in²] | |
| Izod notch impact strength | ASTM D256/ISO 179 | 45（8.4） kg·cm/cm(J/M)ft·lb/in | |
| elongation | ASTM D638/ISO 527 | 40 % | |
| Charpy impact strength | ASTM D256/ISO 179 | - kg·cm/cm(J/M)ft·lb/in | |
| Tensile modulus | ASTM D638/ISO 527 | - kg/cm²(MPa)[Lb/in²] | |
| elongation at break | ASTM D638/ISO 527 | - % | |
| Rockwell hardness | ASTM D785 | R-102 | |
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | - % | |
| tensile strength | ASTM D638/ISO 527 | 400（5，670） kg/cm²(MPa)[Lb/in²] |
| other | Test Condition | Test Method | TAIWAN CHIMEI/PA-709 |
|---|---|---|---|
| 超高耐冲击强度押管用。 | |||
| notes | 在射出周期中勿将热融胶长期停留在加热管中 | ||
| purpose | 水管配件 / 汽车前后扰流板 / 摩托车挡板 / 押出水管 / 安全帽 |
| Physical properties | Test Condition | Test Method | TAIWAN CHIMEI/PA-709 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.03 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 5 g/10min | |
| Mold Shrinkage | ASTM D955 | - % | |
| Water absorption rate | ASTM D570/ISO 62 | - % |
| processability | Test Condition | Test Method | TAIWAN CHIMEI/PA-709 |
|---|---|---|---|
| process temperature | 180~230°C °C | ||
| pressure | - Mpa | ||
| Dry conditions | 80°C下烘料约2~3小时 | ||
| screw speed | - rpm | ||
| Melt Temperature | - °C | ||
| Temperature | 30-70 °C |
| Thermal performance | Test Condition | Test Method | TAIWAN CHIMEI/PA-709 |
|---|---|---|---|
| vicat | ASTM D1525/ISO R306 | 105（221） ℃（℉） | |
| ASTM D648/ISO 75 | 88（190） ℃（℉） | ||
| Combustibility (rate) | UL94 | 1.6mmHB | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | - mm/mm.℃ |