Technical Data Sheet
thermosetting | Test Condition | Test Method | Test Result |
---|
Thermosetting components | Resin | | 按重量计算的混合比:46按容量计算的混合比:4.0 |
Thermosetting components | Hardener | | 按重量计算的混合比:34按容量计算的混合比:3.0 |
Thermosetting components | | | 10to20 min |
Thermosetting components | | | 26 wk |
Thermosetting mixed viscosity | | ASTM D2393 | 750 cP |
stripping time | | | 1400 min |
stripping time | | | 60to120 min |
stripping time | | | 30 min |
hardness | Test Condition | Test Method | Test Result |
---|
Shore hardness | | ASTM D2240 | 7585 |
flammability | Test Condition | Test Method | Test Result |
---|
Limiting Oxygen Index | | ASTM D2863 | 52 % |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
tensile strength | Yield | ASTM D638 | 110 MPa |
elongation | Yield | ASTM D638 | 1.0 % |
elongation | Break | ASTM D638 | 2.2 % |
Flexural modulus | | ASTM D790 | 7580 MPa |
Tensile modulus | | ASTM D638 | 7580 MPa |
bending strength | Yield | ASTM D790 | 207 MPa |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Impact strength of cantilever beam gap | | ASTM D256 | 860 J/m |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | ASTM D648 | 204 °C |
Linear coefficient of thermal expansion | | ASTM D696 | 2.2E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.