PF Fire PRF2 1000 FM Indspec Chemical Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Indspec Chemical Corporation/Fire PRF2 1000 FM |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 860 J/m |
| hardness | Test Condition | Test Method | Indspec Chemical Corporation/Fire PRF2 1000 FM |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 7585 |
| Mechanical properties | Test Condition | Test Method | Indspec Chemical Corporation/Fire PRF2 1000 FM |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 2.2 % |
| 屈服 | ASTM D638 | 1.0 % | |
| bending strength | 屈服 | ASTM D790 | 207 MPa |
| Flexural modulus | ASTM D790 | 7580 MPa | |
| Tensile modulus | ASTM D638 | 7580 MPa | |
| tensile strength | 屈服 | ASTM D638 | 110 MPa |
| thermosetting | Test Condition | Test Method | Indspec Chemical Corporation/Fire PRF2 1000 FM |
|---|---|---|---|
| Thermosetting components | 贮藏期限(22°C) | 26 wk | |
| 储存稳定性(23°C) | 10to20 min | ||
| stripping time | 52°C | 30 min | |
| Thermosetting components | 硬化法 | 按重量计算的混合比:34按容量计算的混合比:3.0 | |
| 树脂 | 按重量计算的混合比:46按容量计算的混合比:4.0 | ||
| stripping time | 23°C | 1400 min | |
| Thermosetting mixed viscosity | 23°C | ASTM D2393 | 750 cP |
| stripping time | 32°C | 60to120 min |
| flammability | Test Condition | Test Method | Indspec Chemical Corporation/Fire PRF2 1000 FM |
|---|---|---|---|
| Limiting Oxygen Index | ASTM D2863 | 52 % |
| Thermal performance | Test Condition | Test Method | Indspec Chemical Corporation/Fire PRF2 1000 FM |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 204 °C |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 2.2E-05 cm/cm/°C |