PC/PBT XENOY™ 5720U-BK1066
88
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Specific volume | ASTM D792 | 0.850 cm³/g | |
| melt mass-flow rate | ASTM D1238 | 3.8 g/10 min | |
| ASTM D1238 | 11 g/10 min | ||
| ASTM D1238 | 6.0 g/10 min | ||
| ASTM D1238 | 20 g/10 min | ||
| ISO 1133 | 3.0 g/10 min | ||
| Melt volume flow rate | ISO 1133 | 3.00 cm3/10min | |
| ISO 1133 | 10.0 cm3/10min | ||
| ISO 1133 | 6.00 cm3/10min | ||
| ISO 1133 | 18.0 cm3/10min | ||
| Shrinkage rate | 内部方法 | 1.0 - 1.2 % | |
| Water absorption rate | ISO 62 | 0.28 % | |
| ISO 62 | 0.080 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 1830 Mpa | |
| 内部方法 | 1830 Mpa | ||
| ASTM D638 | 1810 Mpa | ||
| ISO 527-2/1 | 1790 Mpa | ||
| tensile strength | ASTM D638 | 47.0 Mpa | |
| 内部方法 | 45.0 Mpa | ||
| ASTM D638 | 44.0 Mpa | ||
| ISO 527-2/5 | 44.0 Mpa | ||
| ISO 527-2/50 | 47.0 Mpa | ||
| ASTM D638 | 50.0 Mpa | ||
| 内部方法 | 47.0 Mpa | ||
| ASTM D638 | 48.0 Mpa | ||
| ISO 527-2/5 | 43.0 Mpa | ||
| elongation | ASTM D638 | 4.6 % | |
| 内部方法 | 4.6 % | ||
| ASTM D638 | 4.0 % | ||
| ISO 527-2/5 | 4.1 % | ||
| ISO 527-2/50 | 4.6 % | ||
| ASTM D638 | 120 % | ||
| 内部方法 | 110 % | ||
| ASTM D638 | 120 % | ||
| ISO 527-2/5 | 110 % | ||
| ISO 527-2/50 | 120 % | ||
| Flexural modulus | ASTM D790 | 1660 Mpa | |
| ISO 178 | 1860 Mpa | ||
| bending strength | ISO 178 | 71.0 Mpa | |
| ASTM D790 | 70.0 Mpa | ||
| ASTM D790 | 69.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 47 kJ/m² | |
| ISO 179/1eA | 55 kJ/m² | ||
| Dart impact | ASTM D3763 | 49.0 J | |
| ASTM D3763 | 59.0 J | ||
| ASTM D3763 | 49.0 J | ||
| ASTM D3763 | 61.0 J | ||
| ASTM D3763 | 41.0 J | ||
| ASTM D3763 | 53.0 J | ||
| ASTM D3763 | 44.0 J | ||
| ASTM D3763 | 54.0 J |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 110 °C | ||
| drying time | 4.0 to 6.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 50 to 80 % | ||
| Temperature at the rear of the barrel | 245 to 265 °C | ||
| Temperature in the middle of the barrel | 250 to 270 °C | ||
| Temperature at the front of the material cylinder | 255 to 275 °C | ||
| Spray nozzle temperature | 255 to 270 °C | ||
| Processing (melt) temperature | 260 to 275 °C | ||
| Temperature | 65 to 90 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| screw speed | 50 to 80 rpm | ||
| Exhaust hole depth | 0.013 to 0.020 mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 108 °C | |
| ASTM D648 | 117 °C | ||
| ISO 75-2/Bf | 109 °C | ||
| ASTM D648 | 83.0 °C | ||
| ASTM D648 | 95.0 °C | ||
| ISO 75-2/Af | 87.0 °C | ||
| vicat | ASTM D152513 | 119 °C | |
| ISO 306/B120 | 122 °C | ||
| Linear coefficient of thermal expansion | ASTM E831 | 9.8E-5 cm/cm/°C | |
| ISO 11359-2 | 9.8E-5 cm/cm/°C | ||
| ASTM E831 | 1.0E-4 cm/cm/°C | ||
| ISO 11359-2 | 1.0E-4 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.