Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PBT 5720U-BK1066 SABIC INNOVATIVE US
XENOY™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/5720U-BK1066 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 55 kJ/m² |
| -30°C | ISO 179/1eA | 47 kJ/m² | |
| Dart impact | -40°C, Energy at Peak | ASTM D3763 | 49.0 J |
| -40°C, Total Energy | ASTM D3763 | 59.0 J | |
| -30°C, Total Energy | ASTM D3763 | 61.0 J | |
| -20°C, Energy at Peak | ASTM D3763 | 41.0 J | |
| 23°C, Total Energy | ASTM D3763 | 54.0 J | |
| -30°C, Energy at Peak | ASTM D3763 | 49.0 J | |
| -20°C, Total Energy | ASTM D3763 | 53.0 J | |
| 23°C, Energy at Peak | ASTM D3763 | 44.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/5720U-BK1066 |
|---|---|---|---|
| Tensile modulus | --2 | ASTM D638 | 1830 Mpa |
| tensile strength | 屈服5 | ASTM D638 | 47.0 Mpa |
| elongation | 断裂5 | ASTM D638 | 120 % |
| Flexural modulus | 50.0 mm 跨距8 | ASTM D790 | 1660 Mpa |
| tensile strength | 断裂 | ISO 527-2/5 | 43.0 Mpa |
| Tensile modulus | --4 | ASTM D638 | 1810 Mpa |
| bending strength | 断裂, 50.0 mm 跨距8 | ASTM D790 | 69.0 Mpa |
| elongation | 断裂 | ISO 527-2/50 | 120 % |
| tensile strength | 屈服6 | 内部方法 | 45.0 Mpa |
| elongation | 屈服 | ISO 527-2/5 | 4.1 % |
| tensile strength | 屈服7 | ASTM D638 | 44.0 Mpa |
| 屈服 | ISO 527-2/50 | 47.0 Mpa | |
| 断裂6 | 内部方法 | 47.0 Mpa | |
| bending strength | 屈服, 50.0 mm 跨距8 | ASTM D790 | 70.0 Mpa |
| tensile strength | 断裂7 | ASTM D638 | 50.0 Mpa |
| elongation | 屈服5 | ASTM D638 | 4.0 % |
| tensile strength | 断裂5 | ASTM D638 | 48.0 Mpa |
| elongation | 断裂7 | ASTM D638 | 120 % |
| 断裂 | ISO 527-2/5 | 110 % | |
| 屈服7 | ASTM D638 | 4.6 % | |
| Flexural modulus | --9 | ISO 178 | 1860 Mpa |
| tensile strength | 屈服 | ISO 527-2/5 | 44.0 Mpa |
| bending strength | --9,10 | ISO 178 | 71.0 Mpa |
| elongation | 断裂6 | 内部方法 | 110 % |
| 屈服 | ISO 527-2/50 | 4.6 % | |
| 屈服6 | 内部方法 | 4.6 % | |
| Tensile modulus | --3 | 内部方法 | 1830 Mpa |
| -- | ISO 527-2/1 | 1790 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/5720U-BK1066 |
|---|---|---|---|
| melt mass-flow rate | 250°C/2.16 kg | ASTM D1238 | 3.8 g/10 min |
| 250°C/2.16 kg | ISO 1133 | 3.0 g/10 min | |
| 250°C/5.0 kg | ASTM D1238 | 11 g/10 min | |
| Melt volume flow rate | 250°C/5.0 kg | ISO 1133 | 10.0 cm3/10min |
| 250°C/2.16 kg | ISO 1133 | 3.00 cm3/10min | |
| Shrinkage rate | 3.20 mm，Flow | 内部方法 | 1.0 - 1.2 % |
| Melt volume flow rate | 265°C/5.0 kg | ISO 1133 | 18.0 cm3/10min |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.080 % |
| melt mass-flow rate | 266°C/5.0 kg | ASTM D1238 | 20 g/10 min |
| Melt volume flow rate | 265°C/2.16 kg | ISO 1133 | 6.00 cm3/10min |
| Specific volume | ASTM D792 | 0.850 cm³/g | |
| melt mass-flow rate | 265°C/2.16 kg | ASTM D1238 | 6.0 g/10 min |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.28 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/5720U-BK1066 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 122 °C |
| Heat distortion temperature | 0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距12，HDT | ISO 75-2/Bf | 109 °C |
| Linear coefficient of thermal expansion | 流动 : -40 到 95°C | ASTM E831 | 9.8E-5 cm/cm/°C |
| vicat | -- | ASTM D152513 | 119 °C |
| Linear coefficient of thermal expansion | 横向 : -30 到 80°C | ISO 11359-2 | 1.0E-4 cm/cm/°C |
| Heat distortion temperature | 0.45 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 108 °C |
| 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 95.0 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距12，HDT | ISO 75-2/Af | 87.0 °C | |
| Linear coefficient of thermal expansion | 流动 : -30 到 80°C | ISO 11359-2 | 9.8E-5 cm/cm/°C |
| 横向 : -40 到 95°C | ASTM E831 | 1.0E-4 cm/cm/°C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 117 °C |
| 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 83.0 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/5720U-BK1066 |
|---|---|---|---|
| screw speed | 50 to 80 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Processing (melt) temperature | 260 to 275 °C | ||
| drying temperature | 110 °C | ||
| Suggested injection volume | 50 to 80 % | ||
| drying time | 4.0 to 6.0 hr | ||
| Temperature in the middle of the barrel | 250 to 270 °C | ||
| Temperature at the rear of the barrel | 245 to 265 °C | ||
| Exhaust hole depth | 0.013 to 0.020 mm | ||
| Temperature at the front of the material cylinder | 255 to 275 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 65 to 90 °C | ||
| Spray nozzle temperature | 255 to 270 °C |