Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Apparent density | | ISO60 | 0.65 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 28 g/10min |
| melt mass-flow rate | | ASTMD1238 | 8.0 g/10min |
| melt mass-flow rate | | ISO1133 | 28 g/10min |
| Melt volume-flowrate | | ASTMD1505 | 27.0 cm3/10min |
| Shrinkage rate | | ASTMD955 | 0.40to0.70 % |
| Shrinkage rate | | ISO294-4 | 0.40to0.70 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 108 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Burning rate 8 | | ISO3795 | 60 mm/min |
| UL flame retardant rating 8 | | UL94 | HB |
| UL flame retardant rating 8 | | UL94 | HB |
| Normal combustion performance with a thickness of 1.6mm | | 4.21 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-22 | 2400 Mpa |
| tensile strength | | ASTMD638 | 48.0 Mpa |
| Tensile stress | | ISO527-2/50 | 45.0 Mpa |
| Tensile stress | | ISO527-2/100 | 47.0 Mpa |
| Tensile stress | | ISO527-22 | 48.0 Mpa |
| tensile strength | | ASTMD638 | 35.0 Mpa |
| elongation | | ASTMD638 | 2.7 % |
| Tensile strain | | ISO527-2/50 | 2.5 % |
| Tensile strain | | ISO527-2/100 | 2.6 % |
| elongation | | ASTMD638 | 8.7 % |
| Nominal strainatbreak | | ISO527-22 | 20 % |
| Flexural modulus | | ASTMD790 | 2480 Mpa |
| Bending modulus 5,6 | | ISO178 | 2400 Mpa |
| bending strength | | ASTMD790 | 75.0 Mpa |
| Bending strength 5,6 | | ISO178 | 70.0 Mpa |
| Tensile modulus | | ISO527-2 | 2340 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| CharpyNotchedImpactStrength | | ISO179/1eA2 | 18.0 kJ/m² |
| Charpy impact strength | | ISO179/1eU2 | NoBreak |
| CharpyImpactStrength | | ISO179/1eU2 | NoBreak |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 87.0 °C |
| | ASTMD648 | 74.0 °C |
| | ISO75-2/A | 95.0 °C |
| | ISO75-22 | 95.0 °C |
| vicat | | ASTMD15257 | 99.0 °C |
| vicat | | ISO306/B50 | 95.0 °C |
| vicat | | ISO3062 | 92.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.