Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS 8391 STYRON US
MAGNUM™
Household appliances、Fitness equipment、Toy
High mobility、High gloss、heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | STYRON US/8391 |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eU2 | NoBreak |
| 23°C | ISO 179/1eU2 | NoBreak | |
| 23°C | ISO 179/1eA2 | 18.0 kJ/m² |
| hardness | Test Condition | Test Method | STYRON US/8391 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 108 |
| Mechanical properties | Test Condition | Test Method | STYRON US/8391 |
|---|---|---|---|
| elongation | 屈服 | ASTM D638 | 2.7 % |
| Flexural modulus | 3.20mm,InjectionMolded | ISO 178 | 2400 Mpa |
| Tensile strain | 屈服,3.20mm,注塑 | ISO 527-2/50 | 2.5 % |
| bending strength | ASTM D790 | 75.0 Mpa | |
| tensile strength | 屈服 | ISO 527-22 | 48.0 Mpa |
| 断裂 | ASTM D638 | 35.0 Mpa | |
| Tensile strain | 屈服,3.20mm,注塑 | ISO 527-2/100 | 2.6 % |
| Flexural modulus | ASTM D790 | 2480 Mpa | |
| elongation | 断裂 | ASTM D638 | 8.7 % |
| Tensile modulus | 3.20mm,注塑 | ISO 527-2 | 2340 Mpa |
| Nominal fracture strain | ISO 527-22 | 20 % | |
| bending strength | 3.20mm,InjectionMolded | ISO 178 | 70.0 Mpa |
| tensile strength | 屈服,3.20mm,注塑 | ISO 527-2/50 | 45.0 Mpa |
| 屈服 | ASTM D638 | 48.0 Mpa | |
| 屈服,3.20mm,注塑 | ISO 527-2/100 | 47.0 Mpa | |
| Tensile modulus | ISO 527-22 | 2400 Mpa |
| flammability | Test Condition | Test Method | STYRON US/8391 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| burning rate | 2.00mm | ISO 3795 | 60 mm/min |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Normal combustion performance with a thickness of 1.6mm | 1.50mm,UL | HB 4.21 |
| physical property | Test Condition | Test Method | STYRON US/8391 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.40-0.70 % |
| Melt volume flow rate | 220°C/10.0kg | ASTM D1505 | 27.0 cm3/10min |
| Shrinkage rate | MD | ISO 294-4 | 0.40-0.70 % |
| Apparent density | ISO 60 | 0.65 g/cm³ | |
| melt mass-flow rate | 230°C/3.8kg | ASTM D1238 | 8.0 g/10min |
| 220°C/10.0kg | ASTM D1238 | 28 g/10min | |
| 220°C/10.0kg | ISO 1133 | 28 g/10min |
| Thermal performance | Test Condition | Test Method | STYRON US/8391 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 74.0 °C |
| vicat | 50N | ISO 3062 | 92.0 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 87.0 °C |
| 1.8MPa,退火，HDT | ISO 75-2/A | 95.0 °C | |
| vicat | ISO 306/B50 | 95.0 °C | |
| Heat distortion temperature | 1.8MPa，HDT | ISO 75-22 | 95.0 °C |
| vicat | ASTM D15257 | 99.0 °C |