'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PC/PET XYLEX™ X7507-NA9D032T SABIC INNOVATIVE US
13
Compare
View PricesTechnical Data Sheet
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| transmissivity | 2540 μm | ASTM D1003 | > 85.0 % |
| turbidity | 2540 μm | ASTM D1003 | 1.6 % |
| impact performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | 23°C, Total Energy | ASTM D3763 | 79.0 J |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | Yield, 50.0 mm Span4 | ASTM D790 | 96.0 Mpa |
| --5,6 | ISO 178 | 92.0 Mpa | |
| Bending modulus | --5 | ISO 178 | 2180 Mpa |
| 50.0 mm Span4 | ASTM D790 | 2320 Mpa | |
| elongation | Break | ISO 527-2/50 | 110 % |
| Break3 | ASTM D638 | 130 % | |
| Yield | ISO 527-2/50 | 5.4 % | |
| Yield3 | ASTM D638 | 6.0 % | |
| tensile strength | Break | ISO 527-2/50 | 59.0 Mpa |
| Break3 | ASTM D638 | 65.0 Mpa | |
| Yield | ISO 527-2/50 | 62.0 Mpa | |
| Yield3 | ASTM D638 | 61.0 Mpa | |
| Tensile modulus | -- | ISO 527-2/1 | 2660 Mpa |
| --2 | ASTM D638 | 2300 Mpa |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 80 to 95 °C | ||
| drying time | 3.0 to 5.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 40 to 80 % | ||
| Temperature at the rear of the barrel | 240 to 250 °C | ||
| Temperature in the middle of the barrel | 245 to 265 °C | ||
| Temperature at the front of the material cylinder | 250 to 270 °C | ||
| Spray nozzle temperature | 250 to 270 °C | ||
| Processing (melt) temperature | 250 to 270 °C | ||
| Mold temperature | 45 to 60 °C | ||
| Back pressure | 0.200 to 0.500 Mpa | ||
| Screw speed | 20 to 100 rpm | ||
| Exhaust hole depth | 0.013 to 0.020 mm |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ASTM E831 | 6.0E-5 cm/cm/°C |
| Across Flow : -40 to 40°C | ASTM E831 | 7.0E-5 cm/cm/°C | |
| Across Flow : -40°C | ISO 11359-2 | 6.3E-5 cm/cm/°C | |
| Vicat softening temperature | -- | ISO 306/B120 | 127 °C |
| -- | ASTM D15259 | 125 °C | |
| Hot deformation temperature | 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8 | ISO 75-2/Af | 105 °C |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 104 °C |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | Equilibrium, 23°C, 50% RH | ISO 62 | 0.12 % |
| Saturation, 23°C | ISO 62 | 0.32 % | |
| Shrinkage rate | 3.20 mm，Flow | Internal Method | 0.50 - 0.80 % |
| Melt Volume Flow Rate (MVR) | 265°C/2.16 kg | ISO 1133 | 5.00 cm3/10min |
| melt mass-flow rate | 265°C/2.16 kg | ASTM D1238 | 8.0 g/10 min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.