| physical property | Test Condition | Test Method | Test Result |
|---|
| Apparent density | | JISK6891 | 1.00to1.40 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 10to17 g/10min |
| Water absorption rate | | ASTM D570 | <0.010 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 60to70 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Limiting Oxygen Index | | ASTM D2863 | >95 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D621 | 8.00to9.00 % |
| Heat distortion temperature | | ASTM D621 | 2.00to3.00 % |
| Heat distortion temperature | | ASTM D621 | 8.50to9.50 % |
| bending strength | | ASTM D790 | Nobreak |
| tensile strength | | JISK6891 | 25.4to30.4 Mpa |
| elongation | | JISK6891 | 350to450 % |
| Flexural modulus | | ASTM D790 | 580to690 Mpa |
| Compression Modulus | | ASTM D695 | 490to590 Mpa |
| compressive strength | | ASTM D695 | 4.90to5.90 Mpa |
| compressive strength | | ASTM D695 | 31.4to33.3 Mpa |
| compressive strength | | ASTM D695 | 0.040to0.050 |
| Heat distortion temperature | | ASTM D621 | 2.50to3.00 % |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| melt viscosity | | | 2.00E+6-2.50E+7 mPa·s |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ASTM D4591 | 300to310 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 1.2E-04 cm/cm/°C |
| specific heat | | | 1050 J/kg/°C |
| thermal conductivity | | ASTMC177 | 0.26 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.