PFA AP-210 DAIKIN JAPAN
NEOFLON®
Wire sheath
Weather resistance、Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | DAIKIN JAPAN/AP-210 |
|---|---|---|---|
| Linear thermal expansion coefficient | MD：20到100°C | ASTMD696 | 1.2E-04 cm/cm/°C |
| Specific Heat | 1050 J/kg/°C | ||
| Thermal Conductivity | ASTMC177 | 0.26 W/m/K | |
| Melting temperature | ASTMD4591 | 300到310 °C |
| Fill Analysis | Test Condition | Test Method | DAIKIN JAPAN/AP-210 |
|---|---|---|---|
| Melt Viscosity | 380°C | 2.00E+6到2.50E+7 mPa·s |
| Hardness | Test Condition | Test Method | DAIKIN JAPAN/AP-210 |
|---|---|---|---|
| Shore Hardness | 邵氏D | ASTMD2240 | 60到70 |
| Mechanical Properties | Test Condition | Test Method | DAIKIN JAPAN/AP-210 |
|---|---|---|---|
| Compressive Strength | 25%应变 | ASTMD695 | 31.4到33.3 Mpa |
| 摩擦系数(与钢-静态) | ASTMD695 | 0.040到0.050 | |
| Heat Deflection Temperature | 100°C,6.9MPa3 | ASTMD621 | 8.50到9.50 % |
| 25°C,14MPa2 | ASTMD621 | 2.50到3.00 % | |
| 25°C,14MPa3 | ASTMD621 | 8.00到9.00 % | |
| 100°C,6.9MPa2 | ASTMD621 | 2.00到3.00 % | |
| Flexural Modulus | ASTMD790 | 580到690 Mpa | |
| Flexural Strength | ASTMD790 | Nobreak | |
| Tensile Strength | 屈服 | JISK6891 | 25.4到30.4 Mpa |
| Compressive Strength | 1%应变 | ASTMD695 | 4.90到5.90 Mpa |
| Compressive Modulus | ASTMD695 | 490到590 Mpa | |
| Tensile Elongation | 断裂 | JISK6891 | 350到450 % |
| Physical | Test Condition | Test Method | DAIKIN JAPAN/AP-210 |
|---|---|---|---|
| Melt Mass-Flow Rate | 372°C/5.0kg | ASTMD1238 | 10到17 g/10min |
| Apparent Density | JISK6891 | 1.00到1.40 g/cm³ | |
| Moisture Absorption | 饱和 | ASTMD570 | <0.010 % |
| Flammability | Test Condition | Test Method | DAIKIN JAPAN/AP-210 |
|---|---|---|---|
| Oxygen Index | 1.57mm | ASTMD2863 | >95 % |
| Flame Rating | 1.6mm | UL94 | V-0 |