Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.04 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 20 g/10min |
| Melt volume flow rate | | ISO 1133 | 20.9 cm³/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| DurometerHardness | | ASTM D2240 | 65 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Break | ISO 527-2/50 | 38 % |
| Flexural modulus | | ASTM D790 | 1150 MPa |
| tensile strength | Break | ISO 527-2/50 | 37.0 MPa |
| elongation | Yield | ASTM D638 | 37 % |
| Tensile modulus | | ISO 527-2/1 | 1450 MPa |
| tensile strength | Yield | ASTM D638 | 37.0 MPa |
| tensile strength | Yield | ISO 527-2/50 | 39.0 MPa |
| tensile strength | Break | ASTM D638 | 37.0 MPa |
| Flexural modulus | | ISO 178 | 1260 MPa |
| Tensile strain | Yield | ISO 527-2/50 | 17 % |
| elongation | Break | ASTM D638 | 45 % |
| bending strength | | ISO 178 | 44.0 MPa |
| bending strength | | ASTM D790 | 41.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Dart impact | | ASTM D3763 | 42.0 J |
| Dart impact | | ASTM D3763 | 33.0 J |
| Charpy Notched Impact Strength | | ISO 179/1eA | 43 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D256 | 550 J/m |
| Impact strength of cantilever beam gap | | ISO 180/1A | 9.0 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 41 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| relative permittivity | | IEC 60250 | 2.55 |
| Dissipation Factor | | IEC 60250 | 2E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 115 °C |
| Heat distortion temperature | | ASTM D648 | 84.0 °C |
| Heat distortion temperature | | ISO 75-2/Af | 93.0 °C |
| vicat | | ASTM D15259 | 71.0 °C |
| vicat | | ISO 306/B50 | 71.0 °C |
| vicat | | ISO 306/B120 | 76.0 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 8.2E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTME831 | 1.3E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.