PPO(PPE)+PO NORYL™ WCV065 resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC/NORYL™ WCV065 resin |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 43 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 33.0 J |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 550 J/m |
| Dart impact | -30°C,TotalEnergy | ASTM D3763 | 42.0 J |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 9.0 kJ/m² |
| 23°C | ISO 180/1A | 41 kJ/m² |
| hardness | Test Condition | Test Method | SABIC/NORYL™ WCV065 resin |
|---|---|---|---|
| DurometerHardness | ShoreD,30sec | ASTM D2240 | 65 |
| Mechanical properties | Test Condition | Test Method | SABIC/NORYL™ WCV065 resin |
|---|---|---|---|
| elongation | 屈服 | ASTM D638 | 37 % |
| tensile strength | 屈服 | ASTM D638 | 37.0 MPa |
| Flexural modulus | ISO 178 | 1260 MPa | |
| Tensile strain | 屈服 | ISO 527-2/50 | 17 % |
| tensile strength | 屈服 | ISO 527-2/50 | 39.0 MPa |
| bending strength | ISO 178 | 44.0 MPa | |
| elongation | 断裂 | ASTM D638 | 45 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 41.0 MPa |
| tensile strength | 断裂 | ASTM D638 | 37.0 MPa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 1150 MPa |
| Tensile strain | 断裂 | ISO 527-2/50 | 38 % |
| Tensile modulus | ISO 527-2/1 | 1450 MPa | |
| tensile strength | 断裂 | ISO 527-2/50 | 37.0 MPa |
| Electrical performance | Test Condition | Test Method | SABIC/NORYL™ WCV065 resin |
|---|---|---|---|
| relative permittivity | 1MHz | IEC 60250 | 2.55 |
| Dissipation Factor | 1MHz | IEC 60250 | 2E-03 |
| physical property | Test Condition | Test Method | SABIC/NORYL™ WCV065 resin |
|---|---|---|---|
| Melt volume flow rate | 280°C/5.0kg | ISO 1133 | 20.9 cm³/10min |
| melt mass-flow rate | 280°C/5.0kg | ASTM D1238 | 20 g/10min |
| density | ASTM D792 | 1.04 g/cm³ |
| Thermal performance | Test Condition | Test Method | SABIC/NORYL™ WCV065 resin |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 76.0 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 1.3E-04 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 115 °C |
| vicat | -- | ISO 306/B50 | 71.0 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 8.2E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 93.0 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 84.0 °C | |
| vicat | ASTM D15259 | 71.0 °C |