Polyester, TP DuraStar™ DS1110UVI Eastman Chemical Company

Compare

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
transmissivity	常规	ASTM D1003	89.0 %
transmissivity	transmissivity	Total	ASTM D1003	91.0 %
turbidity		ASTM D1003	0.30 %

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	-40°C	ASTM D4812	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ASTM D4812	无断裂
Dart impact	-40°C,EnergyatPeakLoad	ASTM D3763	48.0 J
	Dart impact	23°C,EnergyatPeakLoad	ASTM D3763	42.0 J
		Dart impact	-40°C,能量to力量峰值	ISO 6603-2	52.6 J
		Dart impact	Dart impact	23°C,能量to力量峰值	ISO 6603-2	58.7 J
Impact strength of cantilever beam gap	-40°C	ASTM D256	40 J/m
	Impact strength of cantilever beam gap	23°C	ASTM D256	80 J/m
		Impact strength of cantilever beam gap	-40°C	ISO 180	4.8 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180	7.8 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	23°C	ISO 527-2	1800 MPa
tensile strength	Yield,23°C	ASTMD638	47.0 MPa
	tensile strength	Break,23°C	ASTM D638	51.0 MPa
	tensile strength	tensile strength	Break,23°C	ISO 527-2	46.0 MPa
elongation	Yield,23°C	ASTM D638	5.0 %
	elongation	Yield,23°C	ISO 527-2	4.0 %
		elongation	Break,23°C	ASTM D638	300 %
		elongation	elongation	Break,23°C	ISO 527-2	200 %
Bending modulus	23°C	ASTM D790	2000 MPa
Bending modulus	Bending modulus	23°C	ISO 178	1850 MPa
bending strength	23°C	ISO 178	65.0 MPa
bending strength	bending strength	Yield,23°C	ASTM D790	69.0 MPa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	75.0 °C
	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	72.0 °C
		Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	65.0 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	66.0 °C

Physical properties	Test Condition	Test Method	Test Result
density	--	ASTM D792	1.20 g/cm³
density	density	23°C	ISO 1183	1.19 g/cm³
Shrinkage rate	MD：3.20mm	ASTM D955	0.20to0.60 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale,23°C	ASTM D785	103

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.