PC 203-22

Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ASTM D792	1.20 g/cm³
	density		ISO 1183/A	1.20 g/cm³
	density	density		ISO 11832	1200 kg/m³
melt mass-flow rate		ASTM D1238	22 g/10min
melt mass-flow rate	melt mass-flow rate		ISO 1133	22 g/10min
Melt volume flow rate		ISO 11332	18.0 cm³/10min
Shrinkage rate		ASTM D955	0.50to0.70 %
Shrinkage rate	Shrinkage rate		ISO 294-4	0.50to0.70 %
Water absorption rate		ASTM D570	0.15 %
	Water absorption rate		ISO 62	0.15 %
		Water absorption rate		ASTM D570	0.32 %
		Water absorption rate	Water absorption rate		ISO 62	0.32 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness		ASTM D785	72
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	118

optical performance	Test Condition	Test Method	Test Result
Haze ratio		ASTM D1003	1.0 %
refractive index		ASTM D542	1.586
refractive index	refractive index		ISO 489	1.586
transmissivity		ASTM D1003	89.0 %

flammability	Test Method	Test Result
UL flame retardant rating	UL 94	HB
Burning Behav.	ISO 12102	HB
Burning Behav.atthicknessh	ISO 12102	HB
Limiting Oxygen Index	ISO 4589-2	26 %
Limiting Oxygen Index (LOI)	ISO 4589-22	26 %
Average degree of combustion	ASTM D635	3 cm
UL flame retardant rating	UL 94	HB

Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	2340 MPa
	Tensile modulus		ISO 527-2/50	2300 MPa
	Tensile modulus	Tensile modulus		ISO 527-22	2300 MPa
tensile strength	Yield	ASTM D638	60.0 MPa
bending strength		ASTM D790	96.5 MPa
bending strength	bending strength		ISO 178	97.0 MPa
Taber abraser		ASTM D1044	45 %
tensile strength	Yield	ISO 527-2/50	60.0 MPa
	tensile strength	Yield	ISO 527-22	60.0 MPa
		tensile strength	Break	ASTM D638	65.5 MPa
		tensile strength	tensile strength	Break	ISO 527-2/50	66.0 MPa
Tensile strain	Yield	ISO 527-22	6.0 %
elongation	Break	ASTM D638	120 %
Tensile strain	Break	ISO 527-2/50	120 %
Nominal fracture strain		ISO 527-22	>50 %
Flexural modulus		ASTM D790	2410 MPa
Flexural modulus	Flexural modulus		ISO 178	2400 MPa

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 179/1eA2	70.0 kJ/m²
	Charpy Notched Impact Strength		ISO 179/1eA2	11.0 kJ/m²
		Charpy Notched Impact Strength		ISO 179/1eU2	NoBreak
		Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179/1eU2	NoBreak
Impact strength of cantilever beam gap		ASTM D256	750 J/m
	Impact strength of cantilever beam gap		ISO 180/A	74 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256	NoBreak
Suspended wall beam without notch impact strength		ISO 180	NoBreak
InstrumentedDartImpact		ASTM D3763	72.3 J
Impact strength of cantilever beam gap		ASTM D1822	378 kJ/m²

Electrical performance	Test Condition	Test Method	Test Result
Dissipation Factor		IEC 602502	1E-03
Dissipation Factor	Dissipation Factor		IEC 602502	2E-03
Compared to the Leakage Tracking Index (CTI)		IEC 60112	PLC 2
Volume resistivity		ASTM D257	2E+17 ohms·cm
Volume resistivity	Volume resistivity		IEC 600932	>1.0E+13 ohms·m
dielectric strength		ASTM D149	17 kV/mm
	dielectric strength		IEC 60243-1	17 kV/mm
	dielectric strength	dielectric strength		IEC 60243-12	17 kV/mm
dielectric constant		ASTM D150	3.00
dielectric constant	dielectric constant		ASTM D150	3.00
relative permittivity		IEC 602502	3.00
relative permittivity	relative permittivity		IEC 602502	3.00
Dissipation Factor		ASTM D150	1E-03
Dissipation Factor	Dissipation Factor		ASTM D150	2E-03

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ASTM D648	139 °C
	Heat distortion temperature		ISO 75-2/A	126 °C
	Heat distortion temperature	Heat distortion temperature		ISO 75-22	128 °C
vicat		ASTM D15257	147 °C
	vicat		ISO 306/B50	147 °C
	vicat	vicat		ISO 3062	147 °C
Ball pressure temperature		IEC 60335-1	125 °C
Linear coefficient of thermal expansion		ASTM D696	6.8E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ISO 11359-22	7E-05 cm/cm/°C
Heat distortion temperature		ASTM D648	126 °C
	Heat distortion temperature		ISO 75-2/B	139 °C
		Heat distortion temperature		ASTM D648	142 °C
			Heat distortion temperature		ISO 75-2/B	142 °C
			Heat distortion temperature	Heat distortion temperature		ISO 75-22	142 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.