PC 203-22 Trinseo
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodTrinseo/ 203-22
Charpy Notched Impact Strength-30°CISO 179/1eU2NoBreak
23°CISO 179/1eU2NoBreak
Impact strength of cantilever beam gap23°CASTM D256750 J/m
InstrumentedDartImpact23°C,TotalEnergyASTM D376372.3 J
Charpy Notched Impact Strength-30°CISO 179/1eA211.0 kJ/m²
Impact strength of cantilever beam gap23°CASTM D256NoBreak
Suspended wall beam without notch impact strength23°CISO 180NoBreak
Impact strength of cantilever beam gapASTM D1822378 kJ/m²
23°CISO 180/A74 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA270.0 kJ/m²
hardnessTest ConditionTest MethodTrinseo/ 203-22
Rockwell hardnessM计秤ASTM D78572
R计秤ASTM D785118
Mechanical propertiesTest ConditionTest MethodTrinseo/ 203-22
Tensile strain屈服ISO 527-226.0 %
tensile strength 屈服ASTM D63860.0 MPa
bending strengthASTM D79096.5 MPa
Flexural modulusISO 1782400 MPa
bending strengthISO 17897.0 MPa
tensile strength 屈服ISO 527-2/5060.0 MPa
Taber abraserASTM D104445 %
elongation断裂ASTM D638120 %
Tensile modulusISO 527-222300 MPa
Nominal fracture strainISO 527-22>50 %
Tensile modulusASTM D6382340 MPa
tensile strength 屈服ISO 527-2260.0 MPa
断裂ASTM D63865.5 MPa
Flexural modulusASTM D7902410 MPa
Tensile modulusISO 527-2/502300 MPa
Tensile strain断裂ISO 527-2/50120 %
tensile strength 断裂ISO 527-2/5066.0 MPa
Electrical performanceTest ConditionTest MethodTrinseo/ 203-22
Dissipation Factor50HzASTM D1501E-03
dielectric strengthIEC 60243-117 kV/mm
dielectric constant60HzASTM D1503.00
Compared to the Leakage Tracking Index (CTI)2.00mm,SolutionAIEC 60112PLC 2
Volume resistivityASTM D2572E+17 ohms·cm
IEC 600932>1.0E+13 ohms·m
Dissipation Factor1MHzASTM D1502E-03
1MHzIEC 6025022E-03
dielectric constant1MHzASTM D1503.00
dielectric strengthASTM D14917 kV/mm
relative permittivity1MHzIEC 6025023.00
Dissipation Factor100HzIEC 6025021E-03
dielectric strengthIEC 60243-1217 kV/mm
relative permittivity100HzIEC 6025023.00
optical performance Test ConditionTest MethodTrinseo/ 203-22
transmissivityASTM D100389.0 %
refractive indexASTM D5421.586
Haze ratioASTM D10031.0 %
refractive indexISO 4891.586
flammabilityTest ConditionTest MethodTrinseo/ 203-22
UL flame retardant rating3.2mmUL 94HB
Burning Behav.atthicknessh3.20mm,ULISO 12102HB
Limiting Oxygen Index (LOI)ISO 4589-2226 %
Average degree of combustionASTM D6353 cm
Limiting Oxygen IndexISO 4589-226 %
Burning Behav.1.60mm,ULISO 12102HB
UL flame retardant rating1.6mmUL 94HB
physical property Test ConditionTest MethodTrinseo/ 203-22
Melt volume flow rate300°C/1.2kgISO 1133218.0 cm³/10min
Shrinkage rateMDASTM D9550.50to0.70 %
MDISO 294-40.50to0.70 %
Water absorption rate平衡,23°C,50%RHASTM D5700.32 %
23°C,24hrISO 620.15 %
平衡,23°C,50%RHISO 620.32 %
densityISO 1183/A1.20 g/cm³
Water absorption rate23°C,24hrASTM D5700.15 %
densityASTM D7921.20 g/cm³
ISO 118321200 kg/m³
melt mass-flow rate300°C/1.2kgASTM D123822 g/10min
300°C/1.2kgISO 113322 g/10min
Thermal performanceTest ConditionTest MethodTrinseo/ 203-22
Heat distortion temperature1.8MPa,未退火，HDTASTM D648126 °C
1.8MPa,退火，HDTASTM D648139 °C
Ball pressure temperatureIEC 60335-1125 °C
vicatISO 306/B50147 °C
Heat distortion temperature1.8MPa，HDTISO 75-22128 °C
Linear coefficient of thermal expansionMD：-40到82°CASTM D6966.8E-05 cm/cm/°C
Heat distortion temperature0.45MPa,退火，HDTISO 75-2/B142 °C
0.45MPa，HDTISO 75-22142 °C
vicatASTM D15257147 °C
50NISO 3062147 °C
Linear coefficient of thermal expansionMDISO 11359-227E-05 cm/cm/°C
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B139 °C
1.8MPa,退火，HDTISO 75-2/A126 °C
0.45MPa,退火，HDTASTM D648142 °C