Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | % | 0.70 0.70 |
| Shrinkage rate | | % | 0.30 0.30 |
| Water absorption rate | | % | 0.90 0.90 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | | 114 102 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | V-0 V-0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | kJ/m² | 45 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | MPa | 12200 |
| Tensile stress | | MPa | 150 113 |
| Tensile strain | | % | 2.1 2.3 |
| Flexural modulus | | MPa | 11000 8200 |
| Bending stress | | MPa | 250 170 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ohms·cm | 1E+15 -- |
| dielectric strength | | kV/mm | 28 -- |
| dielectric constant | | | 3.60 -- |
| Dissipation Factor | | | 0.020 -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | °C | 256 -- |
| | °C | 238 -- |
| | cm/cm/°C | 3E-05 3E-05 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare