Certificates
PA66 BV2120G30 UNITIKA JAPAN
--
Electrical components、Vehicle electronics
Filler: Glass fiber reinf、30%、Filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | UNITIKA JAPAN/BV2120G30 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | kJ/m² | 45 |
| hardness | Test Condition | Test Method | UNITIKA JAPAN/BV2120G30 |
|---|---|---|---|
| Rockwell hardness | R计秤 | 114 102 |
| Electrical performance | Test Condition | Test Method | UNITIKA JAPAN/BV2120G30 |
|---|---|---|---|
| dielectric strength | 1.00mm | kV/mm | 28 -- |
| dielectric constant | 1MHz | 3.60 -- | |
| Volume resistivity | ohms·cm | 1E+15 -- | |
| Dissipation Factor | 1MHz | 0.020 -- |
| Mechanical properties | Test Condition | Test Method | UNITIKA JAPAN/BV2120G30 |
|---|---|---|---|
| Tensile strain | 断裂 | % | 2.1 2.3 |
| bending strength | MPa | 250 170 | |
| Tensile modulus | 12200 MPa | ||
| tensile strength | 断裂 | MPa | 150 113 |
| Flexural modulus | MPa | 11000 8200 |
| flammability | Test Condition | Test Method | UNITIKA JAPAN/BV2120G30 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | V-0 V-0 |
| physical property | Test Condition | Test Method | UNITIKA JAPAN/BV2120G30 |
|---|---|---|---|
| Shrinkage rate | MD:3.20mm | % | 0.30 0.30 |
| Water absorption rate | 平衡,23°C,50%RH | % | 0.90 0.90 |
| Shrinkage rate | TD:3.20mm | % | 0.70 0.70 |
| Thermal performance | Test Condition | Test Method | UNITIKA JAPAN/BV2120G30 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | °C | 256 -- |
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 3E-05 3E-05 |
| Heat distortion temperature | 1.8MPa,未退火，HDT | °C | 238 -- |