Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.06 g/cm³ |
| Shrinkage rate | | ISO 294-4 | 0.9 % |
| Shrinkage rate | | ISO 294-4 | 0.7 % |
| Water absorption rate | | ISO 62 | 6 % |
| Water absorption rate | | ISO 62 | 2.5 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 10 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 15 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 无断裂 |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 无断裂 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | ISO 2039-1 | 120 Mpa |
| Tensile modulus | | ISO 527-2 | 2400 Mpa |
| tensile strength | | ISO 527-2 | 70 Mpa |
| tensile strength | | ISO 527-2 | 50 Mpa |
| Tensile strain | | ISO 527-2 | 6 % |
| Nominal tensile fracture strain | | ISO 527-2 | 15 % |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | UL 94 | HB |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | -- ohms |
| Volume resistivity | | IEC 60093 | 100000000000000 ohms·cm |
| dielectric strength | | IEC 60243-1 | 37 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 135 °C |
| Heat distortion temperature | | ISO 75-2/A | 105 °C |
| Continuous use temperature | | ISO 2578 | 80.0 to 100 °C |
| Continuous use temperature | | 内部方法 | 130 °C |
| melting temperature | | ISO 11357-3 | 220 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 0.000070 1/℃ |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 0.00010 1/℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.