PP Alloy Propafilm™ OLS100 Innovia Films Ltd.
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | 内部方法 | 3.7 % | |
| 内部方法 | 7.0 % | ||
| 内部方法 | 3.5 % | ||
| 内部方法 | 11 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Haze ratio | ASTM D1003 | 1.3 % | |
| gloss | ASTM D2457 | 130 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| coefficient of friction | ASTM D1894 | 0.30 | |
| ASTM D1894 | 0.40 |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Secant modulus | ASTM D882 | 3000 MPa | |
| ASTM D882 | 3600 MPa | ||
| tensile strength | ASTM D882 | 170 MPa | |
| ASTM D882 | 210 MPa | ||
| elongation | ASTM D882 | 120 % | |
| ASTM D882 | 80 % | ||
| Sealing emphasis | 内部方法 | 0.19 N/mm | |
| Initial sealing temperature | 内部方法 | 110to141 °C | |
| OTr | ASTMF1927 | 35 cm³·mm/m²/atm/24hr | |
| Water Vapor Transmission Rate | ASTMF1770 | 0.78 g/m²/24hr | |
| ASTMF1770 | 4.0 g/m²/24hr | ||
| film thickness | 内部方法 | 100 | |
| usage | 内部方法 | 44.1 m²/kg |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.