Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP Alloy Propafilm™ OLS100 Innovia Films Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | Innovia Films Ltd./Propafilm™ OLS100 |
|---|---|---|---|
| usage | 内部方法 | 44.1 m²/kg | |
| elongation | MD:断裂 | ASTM D882 | 120 % |
| Sealing emphasis | 内部方法 | 0.19 N/mm | |
| OTr | 23°C,0%RH | ASTMF1927 | 35 cm³·mm/m²/atm/24hr |
| Secant modulus | 1%正割,MD | ASTM D882 | 3000 MPa |
| Water Vapor Transmission Rate | 38°C,90%RH | ASTMF1770 | 4.0 g/m²/24hr |
| tensile strength | TD:屈服 | ASTM D882 | 210 MPa |
| Secant modulus | 1%正割,TD | ASTM D882 | 3600 MPa |
| film thickness | 内部方法 | 100 | |
| Water Vapor Transmission Rate | 23°C,85%RH | ASTMF1770 | 0.78 g/m²/24hr |
| Initial sealing temperature | 内部方法 | 110to141 °C | |
| tensile strength | MD:屈服 | ASTM D882 | 170 MPa |
| elongation | TD:断裂 | ASTM D882 | 80 % |
| Mechanical properties | Test Condition | Test Method | Innovia Films Ltd./Propafilm™ OLS100 |
|---|---|---|---|
| coefficient of friction | 与自身-静态,外层/外层 | ASTM D1894 | 0.40 |
| 与自身-动态,外层/外层 | ASTM D1894 | 0.30 |
| optical performance | Test Condition | Test Method | Innovia Films Ltd./Propafilm™ OLS100 |
|---|---|---|---|
| gloss | 20° | ASTM D2457 | 130 |
| Haze ratio | ASTM D1003 | 1.3 % |
| physical property | Test Condition | Test Method | Innovia Films Ltd./Propafilm™ OLS100 |
|---|---|---|---|
| Shrinkage rate | MD:80°C,1分钟 | 内部方法 | 3.7 % |
| TD:80°C,1分钟 | 内部方法 | 3.5 % | |
| TD:120°C,1分钟 | 内部方法 | 11 % | |
| MD:120°C,1分钟 | 内部方法 | 7.0 % |