PA6 PA NE 15-1E
0
- Properties:Fillersglass fiber reinforced materials
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 2.3 % | ||
| density | 1.25 g/cm³ | ||
| Shrinkage rate | 0.60到1.0 % | ||
| Water absorption rate | ISO62 | 1.1 % | |
| 7.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile stress | Yield | 140 MPa | |
| Tensile strain | Break | 6.0 % | |
| Flexural modulus | 4900 MPa | ||
| Bending stress | 184 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | 9.0 kJ/m² | ||
| Impact strength of simply supported beam without notch | 40 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | 1E+13 ohms | ||
| Volume resistivity | 1E+17 ohms·cm | ||
| 1E+15 ohms·cm | |||
| dielectric strength | 22到25 kV/mm | ||
| 14到19 kV/mm | |||
| Surface Resistivity | 1E+15 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 150 °C | |||
| melting temperature | 218 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.