PA6 PA NE 15-1E Poly Plastic
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Poly Plastic/ PA NE 15-1E |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 20°C | 40 kJ/m² | |
| Charpy Notched Impact Strength | 20°C | 9.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Poly Plastic/ PA NE 15-1E |
|---|---|---|---|
| Volume resistivity | --3 | 1E+15 ohms·cm | |
| --2 | 1E+17 ohms·cm | ||
| Surface Resistivity | --3 | 1E+13 ohms | |
| --2 | 1E+15 ohms | ||
| dielectric strength | --3 | 14to19 kV/mm | |
| --2 | 22to25 kV/mm |
| Mechanical properties | Test Condition | Test Method | Poly Plastic/ PA NE 15-1E |
|---|---|---|---|
| Flexural modulus | 23°C | 4900 MPa | |
| Tensile strain | 断裂 | 6.0 % | |
| bending strength | 184 MPa | ||
| tensile strength | 屈服 | 140 MPa |
| physical property | Test Condition | Test Method | Poly Plastic/ PA NE 15-1E |
|---|---|---|---|
| Shrinkage rate | 0.60to1.0 % | ||
| density | 1.25 g/cm³ | ||
| Water absorption rate | 饱和,23°C | 7.0 % | |
| 23°C,24hr | ISO 62 | 1.1 % | |
| 平衡,23°C,50%RH | 2.3 % |
| Thermal performance | Test Condition | Test Method | Poly Plastic/ PA NE 15-1E |
|---|---|---|---|
| melting temperature | 218 °C | ||
| Heat distortion temperature | 1.8MPa,未退火，HDT | 150 °C |