DAP

DAP Synres-Almoco DAP 5553 Synres-Almoco BV

Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	Compression Molded	ISO 179/1eA	3.5to6.0 kJ/m²
Impact strength of simply supported beam without notch	Injection	ISO 179/1eU	10to15 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Compression Molded	ISO 179/1eU	5.0to10 kJ/m²
Charpy Notched Impact Strength	Injection	ISO 179/1eA	4.0to8.0 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.60mm	UL 94	V-0
Burning wire flammability index		IEC 60695-2-12	960 °C
Hot filament ignition temperature		IEC 60695-2-13	875 °C

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Injection	ISO 527-2	80.0to100 MPa
Bending modulus	Compression Molded	ISO 178	8000to12000 MPa
Bending modulus	Bending modulus	Injection	ISO 178	12000to18000 MPa
bending strength	Compression Molded	ISO 178	90.0to110 MPa
bending strength	bending strength	Injection	ISO 178	150to180 MPa
Compressive stress		ISO 604	150to200 MPa
Tensile modulus	Compression Molded	ISO 527-2	6000to9000 MPa
tensile strength	CompressionMolded	ISO 527-2	35.0to60.0 MPa
Tensile modulus	Injection	ISO 527-2	10000to16000 MPa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	>180 °C
thermal conductivity		ASTME1461	0.90to1.1 W/m/K
Linear coefficient of thermal expansion	MD：50to100°C	ISO 11359-2	5.0E-6到1.0E-5 cm/cm/°C
Hot deformation temperature	8.0MPa,Unannealed	ISO 75-2/C	120to140 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate		ISO 2577	<0.050 %
Water absorption rate	23°C,24hr	ISO 62	<0.20 %
Shrinkage rate	MD：--4	ISO 2577	0.15to0.45 %
Shrinkage rate	Shrinkage rate	MD：--3	ISO 2577	0.15to0.35 %
Apparent density		ISO 60	0.75to0.90 g/cm³
density		ISO 1183	1.80to2.00 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Arc resistance		ASTM D495	PLC 4
Compared to the anti leakage trace index		IEC 60112	PLC 1
Dissipation factor	1MHz	IEC 60250	0.010to0.030
Dissipation factor	Dissipation factor	100Hz	IEC 60250	0.010to0.030
Relative permittivity	1MHz	IEC 60250	4.004.50
Relative permittivity	Relative permittivity	100Hz	IEC 60250	4.505.00
Dielectric strength		IEC 60243-1	15to20 kV/mm
Volume resistivity		IEC 60093	1.0E+14到1.0E+15 ohms·cm
Surface resistivity		IEC 60093	1.0E+14到1.0E+15 ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.