SMMA NAS® 36 INEOS Barex
0
- Properties:physical property
CompareTechnical Data Sheet
| Test Condition | Test Method | Test Result | |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 0.20to0.60 % | |
| Water absorption rate | ASTM D570 | 0.15 % | |
| ISO 62 | 0.15 % | ||
| Tensile modulus | ASTM D638 | 3240 MPa | |
| ISO 527-2 | 3300 MPa | ||
| Impact strength of cantilever beam gap | ASTM D256 | 21 J/m | |
| ISO 180/A | 2.5 kJ/m² | ||
| Suspended wall beam without notch impact strength | ISO 180 | 12 kJ/m² | |
| Rockwell hardness | M-Scale | ASTM D785 | 75 |
| ball-indentation hardness | ISO 2039-1 | 169 MPa | |
| Heat distortion temperature | ISO 75-2/B | 90.0 °C | |
| tensile strength | ASTM D638 | 60.7 MPa | |
| ISO 527-2 | 60.0 MPa | ||
| elongation | Break | ASTM D638 | 2.3 % |
| Tensile strain | ISO 527-2 | 2.5 % | |
| Flexural modulus | ASTM D790 | 3170 MPa | |
| ISO 178 | 3400 MPa | ||
| bending strength | ASTM D790 | 101 MPa | |
| ISO 178 | 100 MPa | ||
| Charpy Notched Impact Strength | ISO 179 | 1.5 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179 | 12 kJ/m² | |
| refractive index | ASTM D542 | 1.560 | |
| Heat distortion temperature | ISO 75-2/A | 80.0 °C | |
| vicat | ASTM D15253 | 104 °C | |
| ISO 306/B50 | 98.0 °C | ||
| maximum service temperature | 260 °C | ||
| refractive index | ISO 489 | 1.560 | |
| transmissivity | ASTM D1003 | 91.4 % | |
| Haze ratio | ASTM D1003 | 0.30 % | |
| density | ASTM D792 | 1.09 g/cm³ | |
| ISO 1183 | 1.09 g/cm³ | ||
| melt mass-flow rate | ASTM D1238 | 2.2 g/10min | |
| Melt volume flow rate | ISO 1133 | 30.0 cm³/10min | |
| Shrinkage rate | ASTM D955 | 0.20to0.60 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.