Material Comparison

Product Info

Product Name

Brand Name

Usages

Properties

Certificates

SMMA NAS® 36 INEOS Barex

Plastic Datasheets

	Test Condition	Test Method	INEOS Barex/NAS® 36
elongation	断裂	ASTM D638	2.3 %
Tensile modulus		ASTM D638	3240 MPa
Suspended wall beam without notch impact strength		ISO 180	12 kJ/m²
ball-indentation hardness		ISO 2039-1	169 MPa
refractive index		ASTM D542	1.560
density		ISO 1183	1.09 g/cm³
refractive index		ISO 489	1.560
bending strength		ISO 178	100 MPa
vicat		ISO 306/B50	98.0 °C
tensile strength	屈服,23°C	ISO 527-2	60.0 MPa
density		ASTM D792	1.09 g/cm³
Flexural modulus		ASTM D790	3170 MPa
Tensile modulus		ISO 527-2	3300 MPa
Water absorption rate	饱和,23°C	ASTM D570	0.15 %
tensile strength	屈服,23°C	ASTM D638	60.7 MPa
Melt volume flow rate	220°C/10.0kg	ISO 1133	30.0 cm³/10min
Impact strength of simply supported beam without notch	23°C	ISO 179	12 kJ/m²
Rockwell hardness	M级	ASTM D785	75
Impact strength of cantilever beam gap	23°C	ASTM D256	21 J/m
Shrinkage rate	MD	ASTM D955	0.20to0.60 %
maximum service temperature			260 °C
vicat		ASTM D15253	104 °C
Impact strength of cantilever beam gap	23°C	ISO 180/A	2.5 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179	1.5 kJ/m²
Shrinkage rate		ISO 294-4	0.20to0.60 %
transmissivity	550nm	ASTM D1003	91.4 %
Haze ratio		ASTM D1003	0.30 %
melt mass-flow rate	200°C/5.0kg	ASTM D1238	2.2 g/10min
Heat distortion temperature	0.45MPa,未退火，HDT	ISO 75-2/B	90.0 °C
Flexural modulus		ISO 178	3400 MPa
Tensile strain	断裂,23°C	ISO 527-2	2.5 %
Heat distortion temperature	1.8MPa,退火，HDT	ISO 75-2/A	80.0 °C
bending strength		ASTM D790	101 MPa
Water absorption rate	平衡,23°C,50%RH	ISO 62	0.15 %