Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | STM640808 | 0.55 % |
| water content | | ISO960 | 0.15 % |
| density | | ISO1183 | 1.37 g/cm³ |
| melt mass-flow rate | | ISO1133 | 3.0 g/10min |
| Shrinkage rate | | STM640808 | 0.98 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Hot filament ignition temperature | | IEC60695-2-13 | 650 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Yield | ISO527-2 | 2.0 % |
| Flexural modulus | | ISO178 | 8650 MPa |
| Bending stress | | ISO178 | 230 MPa |
| Tensile modulus | | ISO527-2 | 10500 MPa |
| Tensile stress | Yield | ISO527-2 | 180 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179 | 14 kJ/m² |
| Charpy Notched Impact Strength | | ISO179 | 15 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179 | 75 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179 | 80 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 8E+13 ohms |
| Volume resistivity | | IEC60093 | 5E+13 ohms·cm |
| dielectric strength | | IEC60243-1 | 20 kV/mm |
| CTI | | IEC60112 | 575 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 225 °C |
| vicat | | ISO306/B | 215 °C |
| | ISO3146 | 220 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.