PA6 Ultramid® B3ZG6 BK30564
48
- Properties:Oil resistantHigh impact resistanceHigh rigidityImpact modification
- Usages:Automotive sectorIndustrial applicationsLeather suitcaseShell
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO1183 | 1.33 g/cm³ | |
| Melt volume flow rate | ISO1133 | 25.0 cm3/10min | |
| Water absorption rate | ISO62 | 6.2 % | |
| ISO62 | 2.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strain | ISO527-2 | 3.2 % | |
| Flexural modulus | ISO178 | 7900 Mpa | |
| Tensile modulus | ISO527-2 | 8800 Mpa | |
| Tensile stress | ISO527-2 | 150 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO179 | 8.0 kJ/m² | |
| ISO179 | 15 kJ/m² | ||
| Impact strength of cantilever beam gap | ISO180 | 8.0 kJ/m² | |
| ISO180 | 16 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO75-2/A | 205 °C | ||
| ISO3146 | 220 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.