PA6 B3ZG6 BK30564 BASF SHANGHAI
Ultramid®
Automotive sector、Industrial applications、Leather suitcase、Shell
Oil resistant、High impact resistance、High rigidity、Impact modification
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF SHANGHAI/B3ZG6 BK30564 |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ISO180 | 8.0 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179 | 8.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180 | 16 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179 | 15 kJ/m² |
| Mechanical properties | Test Condition | Test Method | BASF SHANGHAI/B3ZG6 BK30564 |
|---|---|---|---|
| Flexural modulus | 23°C | ISO178 | 7900 Mpa |
| Tensile modulus | 23°C | ISO527-2 | 8800 Mpa |
| Tensile strain | 断裂,23°C | ISO527-2 | 3.2 % |
| Tensile stress | 断裂,23°C | ISO527-2 | 150 Mpa |
| physical property | Test Condition | Test Method | BASF SHANGHAI/B3ZG6 BK30564 |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 2.0 % |
| 饱和,23°C | ISO62 | 6.2 % | |
| Melt volume flow rate | 275°C/5.0kg | ISO1133 | 25.0 cm3/10min |
| density | ISO1183 | 1.33 g/cm³ |
| Thermal performance | Test Condition | Test Method | BASF SHANGHAI/B3ZG6 BK30564 |
|---|---|---|---|
| Melting temperature (DSC) | ISO3146 | 220 °C | |
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO75-2/A | 205 °C |