PUR，Unspecified ReoFlex® 40
0
CompareTechnical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|---|---|---|
| STORAGE STABILITY | 30 min | ||
| Thermosetting mixed viscosity | ASTMD2393 | 1500 cP | |
| STORAGE STABILITY | ASTMD2471 | 18 min | |
| stripping time | 960 min | ||
| STORAGE STABILITY | 30 min | ||
| Thermosetting mixed viscosity | ASTMD2393 | 2000 cP | |
| stripping time | 960 min | ||
| 960 min | |||
| STORAGE STABILITY | 20 min | ||
| stripping time | 960 min |
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTMD955 | <0.10 % | |
| ASTMD2393 | Brushable | ||
| density | ASTMD1475 | 1.02 g/cm³ | |
| Specific volume | ASTMD1475 | 0.975 cm³/g | |
| Shrinkage rate | ASTMD2566 | <0.10 % | |
| ASTMD2393 | Brushable | ||
| density | ASTMD1475 | 1.03 g/cm³ | |
| Specific volume | 0.972 cm³/g | ||
| Shrinkage rate | ASTMD955 | <0.10 % | |
| density | ASTMD1475 | 1.02 g/cm³ | |
| Specific volume | 0.983 cm³/g | ||
| Shrinkage rate | ASTMD955 | <0.010 % | |
| density | ASTMD1475 | 1.17 g/cm³ | |
| Specific volume | 0.856 cm³/g |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore A | ASTMD2240 | 40 | |
| Shore A | ASTMD2240 | 40 | |
| Shore A | ASTMD2240 | 40 | |
| Shore A | ASTMD2240 | 40 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Mixing Ratio | 1:1byvolume1:1byweight | ||
| 1:1byvolume1:1byweight | |||
| 1A:1Bbyvolume100A:85Bbyweight | |||
| 1A:1Bbyvolume100A:125Bbyweight |
| elastomer | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tear strength | ASTMD624 | 14.9 kN/m | |
| tensile strength | Break | ASTMD412 | 2.90 MPa |
| elongation | Break | ASTMD412 | 580 % |
| tear strength | ASTMD624 | 11.7 kN/m | |
| Tensile stress | ASTMD412 | 0.689 MPa | |
| tensile strength | Break | ASTMD412 | 3.60 MPa |
| elongation | Break | ASTMD412 | 660 % |
| tear strength | ASTMD624 | 14.4 kN/m | |
| Tensile stress | ASTMD412 | 0.503 MPa | |
| tensile strength | Break | ASTMD412 | 3.38 MPa |
| elongation | Break | ASTMD412 | 1000 % |
| tensile strength | Break | ASTMD412 | 2.07 MPa |
| elongation | Break | ASTMD412 | 1000 % |
| tear strength | ASTMD624 | 10.5 kN/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.