Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Post curing time | | | 3.0to5.0 hr |
| Thermosetting components | Resin | | 100 |
| Thermosetting components | Hardener | | 按重量计算的混合比:22 |
| Post curing time | | | 6.0to8.0 hr |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.10to1.14 g/cm³ |
| Viscosity | | | 0.62to0.82 Pa·s |
| Curing Time | | | 10to12 hr |
| STORAGE STABILITY | | | 35to40 min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 7619 | 84to88 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO 178 | 2900to3400 MPa |
| bending strength | | ISO 178 | 110to130 MPa |
| compression stress | | ISO 604 | 95.0to115 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 41to51 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 90.0to96.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.