Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 0.917 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 2.3 g/10min |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D-2457 | 95 |
| Haze ratio | | ASTM D-1003 | 0.4 % |
| gloss | | ASTMD2457 | 95 |
| Haze ratio | | ASTMD1003 | 0.40 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D-792 | 0.917 g/m3 |
| melt mass-flow rate | | ASTM D-1238 | 2.3 g/10min |
| film thickness | | | 20.3 um |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile yield strength (MD) | | ASTM D-882 | 8.79 Mpa |
| Tensile yield strength (TD) | | ASTM D-882 | 8.16 Mpa |
| Tensile strength at break (MD) | | ASTM D-882 | 20.1 Mpa |
| Tensile fracture strength (TD) | | ASTM D-882 | 28.8 Mpa |
| Tensile elongation at break (MD) | | ASTM D-882 | 460 % |
| Tensile elongation at break (TD) | | ASTM D-882 | 650 % |
| Falling hammer impact | | ASTM D-1709B | 210 g |
| Elmendorf Tear Strength (TD) | | ASTM D-1922 | 510 g |
| Elmendorf Tear Strength (MD) | | ASTM D-1922 | 340 g |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| Film Piercing Resistance Movement | | Internal Method | 22.1 J/cm³ |
| Film Resilience (TD) | | ASTM D-882 | 171 J/cm³ |
| Film Resilience (MD) | | ASTM D-882 | 176 J/cm4 |
| film | Test Condition | Test Method | Test Result |
|---|
| Film thickness - tested | | | 20 µm |
| Membrane puncture resistance | | 内部方法 | 22.1 J/cm³ |
| film strength | | ASTMD882 | 176 J/cm³ |
| film strength | | ASTMD882 | 171 J/cm³ |
| tensile strength | | ASTMD882 | 8.79 Mpa |
| tensile strength | | ASTMD882 | 8.16 Mpa |
| tensile strength | | ASTMD882 | 50.1 Mpa |
| tensile strength | | ASTMD882 | 28.8 Mpa |
| elongation | | ASTMD882 | 460 % |
| elongation | | ASTMD882 | 650 % |
| Falling hammer impact | | ASTMD1709A | 210 g |
| Elmondov tear strength | | ASTMD1922 | 340 g |
| Elmondov tear strength | | ASTMD1922 | 510 g |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ASTM D-1525 | 97.8 °C |
| Melting temperature | | Internal Method | 122 °C |
| vicat | | ASTMD1525 | 97.8 °C |
| | 内部方法 | 122 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.