Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LLDPE 2047G DOW SPAIN
DOWLEX™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | DOW SPAIN/2047G |
|---|---|---|---|
| Film Resilience (MD) | 20.3um | ASTM D-882 | 176 J/cm4 |
| Film Piercing Resistance Movement | 20.3um | Internal Method | 22.1 J/cm³ |
| Film Resilience (TD) | 20.3um | ASTM D-882 | 171 J/cm³ |
| film | Test Condition | Test Method | DOW SPAIN/2047G |
|---|---|---|---|
| tensile strength | MD:断裂,20µm | ASTMD882 | 50.1 Mpa |
| elongation | TD:断裂,20µm | ASTMD882 | 650 % |
| Film thickness - tested | 20 µm | ||
| film strength | TD:20µm | ASTMD882 | 171 J/cm³ |
| Elmondov tear strength | TD:20µm | ASTMD1922 | 510 g |
| Membrane puncture resistance | 20µm | 内部方法 | 22.1 J/cm³ |
| film strength | MD:20µm | ASTMD882 | 176 J/cm³ |
| elongation | MD:断裂,20µm | ASTMD882 | 460 % |
| Falling hammer impact | 20µm | ASTMD1709A | 210 g |
| tensile strength | MD:屈服,20µm | ASTMD882 | 8.79 Mpa |
| Elmondov tear strength | MD:20µm | ASTMD1922 | 340 g |
| tensile strength | TD:断裂,20µm | ASTMD882 | 28.8 Mpa |
| TD:屈服,20µm | ASTMD882 | 8.16 Mpa |
| Basic performance | Test Condition | Test Method | DOW SPAIN/2047G |
|---|---|---|---|
| film thickness | 20.3 um | ||
| density | ASTM D-792 | 0.917 g/m3 | |
| melt mass-flow rate | 190℃/2.16kg | ASTM D-1238 | 2.3 g/10min |
| Mechanical properties | Test Condition | Test Method | DOW SPAIN/2047G |
|---|---|---|---|
| Elmendorf Tear Strength (TD) | 20.3um | ASTM D-1922 | 510 g |
| Tensile elongation at break (MD) | 20.3um | ASTM D-882 | 460 % |
| Tensile fracture strength (TD) | 20.3um | ASTM D-882 | 28.8 Mpa |
| Tensile strength at break (MD) | 20.3um | ASTM D-882 | 20.1 Mpa |
| Tensile yield strength (MD) | 20.3um | ASTM D-882 | 8.79 Mpa |
| Tensile elongation at break (TD) | 20.3um | ASTM D-882 | 650 % |
| Tensile yield strength (TD) | 20.3um | ASTM D-882 | 8.16 Mpa |
| Elmendorf Tear Strength (MD) | 20.3um | ASTM D-1922 | 340 g |
| Falling hammer impact | 20.3um | ASTM D-1709B | 210 g |
| optical performance | Test Condition | Test Method | DOW SPAIN/2047G |
|---|---|---|---|
| gloss | 45°,20.3µm | ASTMD2457 | 95 |
| Haze ratio | 20.3µm | ASTMD1003 | 0.40 % |
| gloss | 45°，20.3um | ASTM D-2457 | 95 |
| Haze ratio | 20.3um | ASTM D-1003 | 0.4 % |
| physical property | Test Condition | Test Method | DOW SPAIN/2047G |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg | ASTMD1238 | 2.3 g/10min |
| density | ASTMD792 | 0.917 g/cm³ |
| Thermal performance | Test Condition | Test Method | DOW SPAIN/2047G |
|---|---|---|---|
| vicat | ASTM D-1525 | 97.8 °C | |
| ASTMD1525 | 97.8 °C | ||
| 内部方法 | 122 °C | ||
| Melting temperature | Internal Method | 122 °C |