COC TOPAS® 9506F-04
816
- Properties:Low water absorptionheat-resisting
- Usages:Wear resistant accessoriesIndustrial Suppliesfilm
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | ISO 1133 | 1.00 cm3/10min | |
| ISO 1133 | 6.00 cm3/10min | ||
| Water absorption rate | ISO 62 | 0.010 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| gloss | ISO 2813 | >100 | |
| Haze ratio | ISO 14782 | <1.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1000 | 2600 Mpa |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-3 | 1700 Mpa | |
| ISO 527-3 | 2000 Mpa | ||
| tensile strength | ISO 527-3 | 55.0 Mpa | |
| ISO 527-3 | 55.0 Mpa | ||
| elongation | ISO 527-3 | 2.9 % | |
| ISO 527-3 | 3.6 % | ||
| Dart impact | ISO 7765-1 | <36 g | |
| Elmendorf tear strength | ISO 6383-2 | 2.3 N | |
| ISO 6383-2 | 2.4 N | ||
| OTr | ASTM D3985 | 17 cm³·mm/m²/atm/24hr | |
| Water Vapor Transmission Rate | ISO 15106-3 | 0.800 g·100µm/(m²·day |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Glass Transition Temperature | ISO 11357-2 | 65.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.