Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
COC 9506F-04 CELANESE USA
TOPAS®
Wear resistant accessorie、Industrial Supplies、film
Low water absorption、heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | CELANESE USA/9506F-04 |
|---|---|---|---|
| Tensile modulus | MD | ISO 527-3 | 1700 Mpa |
| TD | ISO 527-3 | 2000 Mpa | |
| Elmendorf tear strength | TD | ISO 6383-2 | 2.4 N |
| tensile strength | TD:断裂 | ISO 527-3 | 55.0 Mpa |
| elongation | MD:断裂 | ISO 527-3 | 2.9 % |
| Dart impact | ISO 7765-1 | <36 g | |
| tensile strength | MD:断裂 | ISO 527-3 | 55.0 Mpa |
| elongation | TD:断裂 | ISO 527-3 | 3.6 % |
| OTr | 23°C,50%RH | ASTM D3985 | 17 cm³·mm/m²/atm/24hr |
| Water Vapor Transmission Rate | 38°C | ISO 15106-3 | 0.800 g·100µm/(m²·day |
| Elmendorf tear strength | MD | ISO 6383-2 | 2.3 N |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/9506F-04 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1000 | 2600 Mpa |
| optical performance | Test Condition | Test Method | CELANESE USA/9506F-04 |
|---|---|---|---|
| Haze ratio | ISO 14782 | <1.0 % | |
| gloss | 60° | ISO 2813 | >100 |
| physical property | Test Condition | Test Method | CELANESE USA/9506F-04 |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 1.00 cm3/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.010 % |
| Melt volume flow rate | 230°C/2.16kg | ISO 1133 | 6.00 cm3/10min |
| Thermal performance | Test Condition | Test Method | CELANESE USA/9506F-04 |
|---|---|---|---|
| Glass Transition Temperature | ISO 11357-2 | 65.0 °C |