Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
density | | ASTM D792 | 1.20 g/cm³ |
melt mass-flow rate | | ASTM D1238 | 15 g/10min |
Shrinkage rate | | 内部方法 | 0.40to0.80 % |
Water absorption rate | | 内部方法 | 0.15 % |
flammability | Test Condition | Test Method | Test Result |
---|
Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
Hot filament ignition temperature | | IEC 60695-2-13 | 875 °C |
Hot filament ignition temperature | | IEC 60695-2-13 | 875 °C |
UL flame retardant rating | | UL 94 | HB |
Burning wire flammability index | | IEC 60695-2-12 | 850 °C |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Impact strength of cantilever beam gap | | ASTM D256 | 650 J/m |
Impact strength of cantilever beam gap | | ASTM D256 | 700 J/m |
Impact strength of cantilever beam gap | | ASTM D256 | 800 J/m |
Dart impact | | ASTM D3763 | 70.0 J |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
tensile strength | Yield | ASTM D638 | 57.0 MPa |
tensile strength | Break | ASTM D638 | 55.0 MPa |
elongation | Yield | ASTM D638 | 6.0 % |
elongation | Break | ASTM D638 | 100 % |
Flexural modulus | | ASTM D790 | 2100 MPa |
bending strength | | ASTM D790 | 90.0 MPa |
Tensile modulus | | ASTM D638 | 2200 MPa |
Electrical performance | Test Condition | Test Method | Test Result |
---|
Surface Resistivity | | ASTM D257 | >1.0E+15 ohms |
Volume resistivity | | ASTM D257 | >1.0E+15 ohms·cm |
dielectric strength | | ASTM D149 | 15 kV/mm |
dielectric constant | | ASTM D150 | 3.00 |
Dissipation Factor | | ASTM D150 | 9.2E-03 |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | ASTM D648 | 123 °C |
vicat | | ASTM D15256 | 145 °C |
Linear coefficient of thermal expansion | | ASTME831 | 6E-05 cm/cm/°C |
Linear coefficient of thermal expansion | | ASTME831 | 6E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.