PC LEXAN™ EXL8134 resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC/LEXAN™ EXL8134 resin |
|---|---|---|---|
| Impact strength of cantilever beam gap | -40°C | ASTM D256 | 650 J/m |
| -30°C | ASTM D256 | 700 J/m | |
| 23°C | ASTM D256 | 800 J/m | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 70.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC/LEXAN™ EXL8134 resin |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 100 % |
| 屈服 | ASTM D638 | 6.0 % | |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 90.0 MPa |
| tensile strength | 断裂 | ASTM D638 | 55.0 MPa |
| Tensile modulus | ASTM D638 | 2200 MPa | |
| tensile strength | 屈服 | ASTM D638 | 57.0 MPa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2100 MPa |
| Electrical performance | Test Condition | Test Method | SABIC/LEXAN™ EXL8134 resin |
|---|---|---|---|
| dielectric strength | 0.800mm,inOil | ASTM D149 | 15 kV/mm |
| Volume resistivity | ASTM D257 | >1.0E+15 ohms·cm | |
| Surface Resistivity | ASTM D257 | >1.0E+15 ohms | |
| Dissipation Factor | 1MHz | ASTM D150 | 9.2E-03 |
| dielectric constant | 1MHz | ASTM D150 | 3.00 |
| flammability | Test Condition | Test Method | SABIC/LEXAN™ EXL8134 resin |
|---|---|---|---|
| Hot filament ignition temperature | 3.00mm | IEC 60695-2-13 | 875 °C |
| UL flame retardant rating | 0.750mm | UL 94 | HB |
| Burning wire flammability index | 3.00mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 1.00mm | IEC 60695-2-13 | 875 °C |
| Burning wire flammability index | 1.00mm | IEC 60695-2-12 | 850 °C |
| physical property | Test Condition | Test Method | SABIC/LEXAN™ EXL8134 resin |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40to0.80 % |
| Water absorption rate | 23°C,24hr | 内部方法 | 0.15 % |
| density | ASTM D792 | 1.20 g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 15 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC/LEXAN™ EXL8134 resin |
|---|---|---|---|
| vicat | ASTM D15256 | 145 °C | |
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 6E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 123 °C |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 6E-05 cm/cm/°C |