PBT VALOX™ K4560 1001 SABIC INNOVATIVE SHANGHAI
131
- Properties:High rigidityhigh strength
- Usages:Home appliance componentsAutomotive Applications
CompareTechnical Data Sheet
| 物理性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 熔体体积流动速率 | 250°C/5.0kg | ISO1133 | 41.0 cm3/10min |
| 收缩率 | MD：3.20mm | 内部方法 | 0.60to0.80 % |
| TD：3.20mm | 内部方法 | 1.0to1.2 % |
| 热性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 热变形温度 | 0.45MPa,未退火,3.20mm | ASTMD648 | 220 °C |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 200 °C |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 弯曲模量9 | 50.0mm跨距4 | ASTMD790 | 8000 Mpa |
| 50.0mm跨距 | ASTMD790 | 7200 Mpa | |
| 50.0mm跨距7 | ASTMD790 | 7400 Mpa | |
| FlexuralStrength9 | Break,50.0mmSpan | ASTMD790 | 173 Mpa |
| 拉伸模量 | ASTMD638 | 8840 Mpa | |
| 抗张强度 | 屈服 | ASTMD638 | 112 Mpa |
| Break3,4 | ASTMD638 | 107 Mpa | |
| Break3,5 | ASTMD638 | 115 Mpa | |
| Break3,6 | ASTMD638 | 110 Mpa | |
| 断裂3 | ASTMD638 | 112 Mpa | |
| Break3,7 | ASTMD638 | 102 Mpa | |
| Break8,7 | ASTMD638 | 96.0 Mpa | |
| 伸长率 | 屈服 | ASTMD638 | 4.0 % |
| 屈服 | ASTMD638 | 3.0 % | |
| 断裂4 | ASTMD638 | 2.5 % | |
| 断裂 | ASTMD638 | 3.0 % | |
| 断裂 | ASTMD638 | 4.0 % | |
| 断裂7 | ASTMD638 | 2.2 % | |
| 弯曲模量9 | 50.0mm跨距5 | ASTMD790 | 7100 Mpa |
| 50.0mm跨距6 | ASTMD790 | 7500 Mpa |
| 冲击性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 装有测量仪表的落镖冲击 | 23°C,TotalEnergy4 | ASTMD3763 | 6.10 J |
| 23°C,TotalEnergy5 | ASTMD3763 | 7.56 J | |
| 23°C,TotalEnergy7 | ASTMD3763 | 8.81 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.