Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT K4560 1001 SABIC INNOVATIVE SHANGHAI
VALOX™
Home appliance components、Automotive Applications
High rigidity、high strength
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/K4560 1001 |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 220 °C |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 200 °C |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/K4560 1001 |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 7200 Mpa |
| Tensile Elongation | 断裂7 | ASTMD638 | 2.2 % |
| 断裂4 | ASTMD638 | 2.5 % | |
| Tensile Strength | 断裂3 | ASTMD638 | 112 Mpa |
| Tensile Elongation | 断裂 | ASTMD638 | 4.0 % |
| Tensile Strength | Break3,7 | ASTMD638 | 102 Mpa |
| Break3,6 | ASTMD638 | 110 Mpa | |
| Break3,5 | ASTMD638 | 115 Mpa | |
| Break8,7 | ASTMD638 | 96.0 Mpa | |
| 屈服 | ASTMD638 | 112 Mpa | |
| Flexural Modulus | 50.0mm跨距5 | ASTMD790 | 7100 Mpa |
| 50.0mm跨距6 | ASTMD790 | 7500 Mpa | |
| 50.0mm跨距4 | ASTMD790 | 8000 Mpa | |
| Tensile Strength | Break3,4 | ASTMD638 | 107 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 3.0 % |
| Flexural Strength | Break,50.0mmSpan | ASTMD790 | 173 Mpa |
| Tensile Modulus | ASTMD638 | 8840 Mpa | |
| Flexural Modulus | 50.0mm跨距7 | ASTMD790 | 7400 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/K4560 1001 |
|---|---|---|---|
| Melt Volume flow Rate | 250°C/5.0kg | ISO1133 | 41.0 cm3/10min |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.60to0.80 % |
| TD：3.20mm | 内部方法 | 1.0to1.2 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/K4560 1001 |
|---|---|---|---|
| Instrumented Dart Impact | 23°C,TotalEnergy7 | ASTMD3763 | 8.81 J |
| 23°C,TotalEnergy4 | ASTMD3763 | 6.10 J | |
| 23°C,TotalEnergy5 | ASTMD3763 | 7.56 J |