PCTG Eastar™ DN003 EASTMAN USA

Properties:
Chemical resistanceHydrolysis resistance
Usages:
Electrical applicationsHousehold daily necessities
Certificates:
UL
Compare View Prices

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Multi axis Instrumented Impact Energy	23°C,能量to力量峰值	ISO 6603-2	14.0 J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	-40°C,能量to力量峰值	ISO 6603-2	16.0 J
Impact strength of cantilever beam gap	23°C	ASTM D4218	NoBreak
	Impact strength of cantilever beam gap	-40°C	ASTM D4218	NoBreak
		Impact strength of cantilever beam gap	23°C	ISO 180	130 kJ/m²
			Impact strength of cantilever beam gap	-40°C	ASTM D256	64 J/m
				Impact strength of cantilever beam gap	23°C	ASTM D256	NoBreak
				Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-40°C	ISO 180	7.4 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	3.2mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.6mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
elongation	Yield,23°C	ASTM D638	5.0 %
tensile strength	Break,23°C,4.00mm	ISO 527-2	47.0 Mpa
	tensile strength	Break,23°C	ASTM D638	52.0 Mpa
		tensile strength	Yield,23°C,4.00mm	ISO 527-2	46.0 Mpa
		tensile strength	tensile strength	Yield,23°C	ASTM D638	45.0 Mpa
Tensile strain	Yield,23°C,4.00mm	ISO 527-2	4.4 %
elongation	Break,23°C	ASTM D638	330 %
Tensile strain	Break,23°C,4.00mm	ISO 527-2	230 %
Bending modulus	23°C	ASTM D790	1800 Mpa
Bending modulus	Bending modulus	23°C,4.00mm	ISO 178	1800 Mpa
bending strength	23°C,4.00mm	ISO 178	63.0 Mpa
bending strength	bending strength	Yield,23°C	ASTM D790	66.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	74.0 °C
	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	74.0 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	64.0 °C
specific heat	导热系数(23°C)	DSC	0.19 W/m/K
Vicat softening temperature		ASTM D15252	88.0 °C
specific heat	240°C	DSC	2050 J/kg/°C
specific heat	specific heat	60°C	DSC	1340 J/kg/°C
Vicat softening temperature	--	ISO 306/B	79.0 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/A	88.0 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	65.0 °C

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792	1.23 g/cm³
Water absorption rate	23°C,24hr	ISO 62	0.13 %
Water absorption rate	Water absorption rate	23°C,24hr	ASTM D570	0.13 %
Shrinkage rate	MD：3.20mm	ASTM D955	0.20-0.50 %
density	23°C	ISO 1183	1.23 g/cm³

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Sale,23°C	ASTM D785	105

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.