PCTG DN003 EASTMAN USA
Eastar™
Electrical applications、Household daily necessiti
Chemical resistance、Hydrolysis resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | EASTMAN USA/DN003 |
|---|---|---|---|
| Impact strength of cantilever beam gap | -40°C | ASTM D256 | 64 J/m |
| Multi axis Instrumented Impact Energy | -40°C,能量到力量峰值 | ISO 6603-2 | 16.0 J |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 130 kJ/m² |
| 23°C | ASTM D4218 | NoBreak | |
| 23°C | ASTM D256 | NoBreak | |
| -40°C | ISO 180 | 7.4 kJ/m² | |
| -40°C | ASTM D4218 | NoBreak | |
| Multi axis Instrumented Impact Energy | 23°C,能量到力量峰值 | ISO 6603-2 | 14.0 J |
| hardness | Test Condition | Test Method | EASTMAN USA/DN003 |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ASTM D785 | 105 |
| Mechanical properties | Test Condition | Test Method | EASTMAN USA/DN003 |
|---|---|---|---|
| tensile strength | Yield,23°C,4.00mm | ISO 527-2 | 46.0 Mpa |
| Flexural modulus | 23°C,4.00mm | ISO 178 | 1800 Mpa |
| Tensile strain | Break,23°C,4.00mm | ISO 527-2 | 230 % |
| bending strength | 23°C,4.00mm | ISO 178 | 63.0 Mpa |
| tensile strength | 屈服,23°C | ASTM D638 | 45.0 Mpa |
| Break,23°C,4.00mm | ISO 527-2 | 47.0 Mpa | |
| elongation | 屈服,23°C | ASTM D638 | 5.0 % |
| tensile strength | 断裂,23°C | ASTM D638 | 52.0 Mpa |
| bending strength | 屈服,23°C | ASTM D790 | 66.0 Mpa |
| Flexural modulus | 23°C | ASTM D790 | 1800 Mpa |
| Tensile strain | Yield,23°C,4.00mm | ISO 527-2 | 4.4 % |
| elongation | 断裂,23°C | ASTM D638 | 330 % |
| flammability | Test Condition | Test Method | EASTMAN USA/DN003 |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | EASTMAN USA/DN003 |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.23 g/cm³ |
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.20-0.50 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.13 % |
| 23°C,24hr | ASTM D570 | 0.13 % | |
| density | ASTM D792 | 1.23 g/cm³ |
| Thermal performance | Test Condition | Test Method | EASTMAN USA/DN003 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 64.0 °C |
| specific heat | 60°C | DSC | 1340 J/kg/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 74.0 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 74.0 °C | |
| specific heat | 导热系数(23°C) | DSC | 0.19 W/m/K |
| vicat | ASTM D15252 | 88.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 65.0 °C |
| specific heat | 240°C | DSC | 2050 J/kg/°C |
| vicat | -- | ISO 306/B | 79.0 °C |
| -- | ISO 306/A | 88.0 °C |