Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.24到1.26 g/cm³ |
| melt mass-flow rate | | ISO1133 | 10 g/10min |
| Shrinkage rate | | 内部方法 | 0.20到0.40 % |
| Water absorption rate | | ISO62 | 0.10 % |
| Water absorption rate | | ISO62 | 0.25 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Burning wire flammability index | | IEC60695-2-12 | 650 °C |
| Limiting Oxygen Index | | ASTMD2863 | 24 % |
| UL flame retardant rating | | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ReinforcementContent | | ISO3451 | 20 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/1 | 6000 MPa |
| Tensile stress | Break | ISO527-2/50 | 75.0 MPa |
| Tensile strain | Break | ISO527-2/50 | 2.0 % |
| Flexural modulus | | ISO178 | 5200 MPa |
| Bending stress | | ISO178 | 110 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 10 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 30 kJ/m² |
| Impact strength of cantilever beam gap | | ASTMD256 | 100 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC60093 | >1.0E+15 ohms·cm |
| dielectric strength | | IEC60243-1 | 24 kV/mm |
| CTI | | IEC60112 | 200 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 118 °C |
| vicat | | ISO306/B50 | 134 °C |
| BallPressure Test | | IEC60695-10-2 | 通过 |
| | ISO11359-2 | 4E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare