Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS TAROBLEND 88 G4 Taro Plast S.p.A.
--
--
Filler, glass fiber reinforced material, 20%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 88 G4 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 100 J/m |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 30 kJ/m² |
| Supplementary Information | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 88 G4 |
|---|---|---|---|
| ReinforcementContent | 750°C | ISO 3451 | 20 % |
| Mechanical properties | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 88 G4 |
|---|---|---|---|
| Flexural modulus | ISO 178 | 5200 MPa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 2.0 % |
| Tensile modulus | ISO 527-2/1 | 6000 MPa | |
| bending strength | ISO 178 | 110 MPa | |
| tensile strength | 断裂 | ISO 527-2/50 | 75.0 MPa |
| Electrical performance | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 88 G4 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | 2.00mm | IEC 60243-1 | 24 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 3 |
| flammability | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 88 G4 |
|---|---|---|---|
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 650 °C |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| Limiting Oxygen Index | ASTM D2863 | 24 % |
| physical property | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 88 G4 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.20to0.40 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.10 % |
| melt mass-flow rate | 260°C/5.0kg | ISO 1133 | 10 g/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.25 % |
| density | ISO 1183 | 1.24to1.26 g/cm³ |
| Thermal performance | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 88 G4 |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：-30到30°C | ISO 11359-2 | 4E-05 cm/cm/°C |
| vicat | ISO 306/B50 | 134 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 118 °C |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | 通过 |