Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.14 -- |
| Shrinkage rate | | % | 0.50 -- |
| Shrinkage rate | | % | 0.10 -- |
| Water absorption rate | | % | 5.5 -- |
| Water absorption rate | | % | 2.0 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | MPa | 150 90.0 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | | HB -- |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | kJ/m² | 55 60 |
| Charpy Notched Impact Strength | | kJ/m² | 5.0 5.0 |
| Charpy Notched Impact Strength | | kJ/m² | 10 12 |
| Impact strength of simply supported beam without notch | | kJ/m² | 60 60 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | MPa | 5500 4000 |
| tensile strength | Break | MPa | 105 70.0 |
| Tensile strain | Break | % | 4.0 10 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ohms | -- 1E+12 |
| Volume resistivity | | ohms·cm | 1E+14 1E+13 |
| dielectric strength | | kV/mm | 38 32 |
| Compared to the Leakage Tracking Index (CTI) | | V | -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | °C | 160 -- |
| Heat distortion temperature | | °C | 65.0 -- |
| Continuous use temperature | | °C | 80.0to110 -- |
| Continuous use temperature | | °C | 160 -- |
| melting temperature | | °C | 222 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 2E-05 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 1.3E-04 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.