| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 0.930 g/cm³ |
| density | | ASTM D792 | 0.950 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 81 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | ISO 3795 | 32 mm/min |
| atomization | | SAEJ1756 | 98 % |
| atomization | | SAEJ1756 | 98 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ArizonaWeather | | SAEJ1976 | 0.220Pass(Blackonly) |
| FloridaWeather | | SAEJ1976 | 0.330Pass(Blackonly) |
| WeatherResistance | | SAEJ1885 | 0.570Pass(Blackonly) |
| WeatherResistance | | SAEJ1960 | 0.300Pass(Blackonly) |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | Break | ISO 37 | 640 % |
| tear strength | | ISO 34-1 | 39 kN/m |
| compression set | | ASTM D395 | 43 % |
| compression set | | ASTM D395 | 58 % |
| atomization | | SAE J1756 | > 98 % |
| atomization | | SAE J1756 | > 98 % |
| Change rate of tensile strength in air | | ASTM D412 | -3.0 % |
| Change rate of ultimate elongation in air | | ASTM D412 | -15 % |
| Shore hardness | | ASTM D2240 | 80 |
| tensile strength | | ISO 37 | 3.50 MPa |
| tensile strength | Yield | ISO 37 | 8.20 MPa |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 37 | 3.80 MPa |
| tensile strength | Yield | ISO 37 | 13.7 MPa |
| elongation | Break | ISO 37 | 900 % |
| tear strength | | ISO 34-1 | 51 kN/m |
| compression set | | ASTM D395 | 43 % |
| compression set | | ASTM D395 | 58 % |
| aging | Test Condition | Test Method | Test Result |
|---|
| Change rate of tensile strength in air | | ASTM D573 | -3.0 % |
| elongation at break | | ASTM D573 | -15 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| cold flexibility | | | No cracks |
| burning rate | | FMVSS 302 | 130 mm/min |
| Low temperature bendability | | FLTMBN102-01 | Pass |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.