Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
TPE 3582-80A USA Weikai
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | USA Weikai/3582-80A |
|---|---|---|---|
| Shore hardness | 邵氏A,15秒 | ASTM D2240 | 81 |
| Supplementary Information | Test Condition | Test Method | USA Weikai/3582-80A |
|---|---|---|---|
| WeatherResistance | --4 | SAEJ1885 | 0.570Pass(Blackonly) |
| FloridaWeather | SAEJ1976 | 0.330Pass(Blackonly) | |
| WeatherResistance | --5 | SAEJ1960 | 0.300Pass(Blackonly) |
| ArizonaWeather | SAEJ1976 | 0.220Pass(Blackonly) |
| Mechanical properties | Test Condition | Test Method | USA Weikai/3582-80A |
|---|---|---|---|
| elongation | 断裂 | ISO 37 | 640 % |
| Change rate of tensile strength in air | 80℃, 1008 hr | ASTM D412 | -3.0 % |
| Shore hardness | 邵氏 A, 15 秒 | ASTM D2240 | 80 |
| tensile strength | 100%应变 | ISO 37 | 3.50 MPa |
| atomization | 38℃ | SAE J1756 | > 98 % |
| Change rate of ultimate elongation in air | 80℃, 1008 hr | ASTM D412 | -15 % |
| compression set | 23℃, 168 hr | ASTM D395 | 43 % |
| atomization | 95℃ | SAE J1756 | > 98 % |
| tear strength | ISO 34-1 | 39 kN/m | |
| compression set | 100℃, 168 hr | ASTM D395 | 58 % |
| tensile strength | 屈服 | ISO 37 | 8.20 MPa |
| flammability | Test Condition | Test Method | USA Weikai/3582-80A |
|---|---|---|---|
| atomization | 95°C | SAEJ1756 | 98 % |
| burning rate | ISO 3795 | 32 mm/min | |
| atomization | 38°C | SAEJ1756 | 98 % |
| elastomer | Test Condition | Test Method | USA Weikai/3582-80A |
|---|---|---|---|
| tensile strength | 100%应变 | ISO 37 | 3.80 MPa |
| compression set | 23°C,168hr | ASTM D395 | 43 % |
| 100°C,168hr | ASTM D395 | 58 % | |
| elongation | 断裂 | ISO 37 | 900 % |
| tensile strength | 屈服 | ISO 37 | 13.7 MPa |
| tear strength | ISO 34-1 | 51 kN/m |
| aging | Test Condition | Test Method | USA Weikai/3582-80A |
|---|---|---|---|
| Change rate of tensile strength in air | 100°C,1008hr | ASTM D573 | -3.0 % |
| elongation at break | 100°C,1008hr | ASTM D573 | -15 % |
| physical property | Test Condition | Test Method | USA Weikai/3582-80A |
|---|---|---|---|
| density | ASTM D792 | 0.950 g/cm³ |
| Thermal performance | Test Condition | Test Method | USA Weikai/3582-80A |
|---|---|---|---|
| burning rate | FMVSS 302 | 130 mm/min | |
| cold flexibility | -30℃ | No cracks | |
| Low temperature bendability | -30°C | FLTMBN102-01 | Pass |