Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D955 | 1.6 - 1.8 % |
| Shrinkage rate | | 内部方法 | 1.1 - 1.3 % |
| Shrinkage rate | | 内部方法 | 1.0 - 1.2 % |
| Water absorption rate | | ASTM D570 | 0.50 % |
| Water absorption rate | | ASTM D570 | 1.0 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 116 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 59.0 Mpa |
| tensile strength | | ASTM D638 | 55.0 Mpa |
| elongation | | ASTM D638 | 60 % |
| Flexural modulus | | ASTM D790 | 2240 Mpa |
| bending strength | | ASTM D790 | 95.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Dart impact | | ASTM D3763 | 39.0 J |
| Dart impact | | ASTM D3763 | 50.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| arc resistance | | ASTM D495 | PLC 7 |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 1 |
| High arc combustion index (HAI) | | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 4 |
| Hot wire ignition (HWI) | | UL 746 | PLC 3 |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 95 to 105 °C |
| drying time | | | 3.0 to 4.0 hr |
| Suggested maximum moisture content | | | 0.070 % |
| Suggested injection volume | | | 30 to 50 % |
| Temperature at the rear of the barrel | | | 265 to 305 °C |
| Temperature in the middle of the barrel | | | 270 to 305 °C |
| Temperature at the front of the material cylinder | | | 275 to 305 °C |
| Spray nozzle temperature | | | 280 to 305 °C |
| Processing (melt) temperature | | | 280 to 305 °C |
| Temperature | | | 75 to 120 °C |
| Back pressure | | | 0.300 to 1.40 Mpa |
| screw speed | | | 20 to 100 rpm |
| Exhaust hole depth | | | 0.013 to 0.038 mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 193 °C |
| Heat distortion temperature | | ASTM D648 | 143 °C |
| vicat | | ASTM D15254 | 232 °C |
| Linear coefficient of thermal expansion | | ASTM E831 | 9.0E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTM E831 | 1.3E-4 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTM E831 | 9.0E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTM E831 | 1.3E-4 cm/cm/°C |
| RTI Elec | | UL 746 | 50.0 °C |
| RTI Imp | | UL 746 | 50.0 °C |
| RTI | | UL 746 | 50.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.