PC/ABS CA3250 BK08011
33
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Specific gravity 23 ℃ | 1.18 g/cm³ | ||
| Shrinkage rate flow 2.0mm | 0.5-0.7 % | ||
| 17 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus 1 Omm/min | 2300 Mpa | ||
| Tensile strength 50mm/min | 60 Mpa | ||
| Elongation fracture 50mm/min | 50 % | ||
| Bending strength 2.0mm/min | 90 Mpa | ||
| 2400 Mpa | |||
| Cantilever beam notch impact at 23 ℃ | 600 J/m |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Fire rating 1.5mm | V-0 | ||
| Fire rating 3.0mm | V-0 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 10000000000000000 Q.cm | |||
| Surface Resistivity | 1000000000000000 Q |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature 1.8MPa120 ℃/hr | 82 °C | ||
| Vicat softening temperature 120 ℃/hr 50N | 102 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.