PC/ABS CA3250 BK08011 YANTAI WANHUA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | YANTAI WANHUA/CA3250 BK08011 |
|---|---|---|---|
| Bending strength 2.0mm/min | 90 Mpa | ||
| Cantilever beam notch impact at 23 ℃ | 600 J/m | ||
| 2400 Mpa | |||
| Elongation fracture 50mm/min | 50 % | ||
| Tensile modulus 1 Omm/min | 2300 Mpa | ||
| Tensile strength 50mm/min | 60 Mpa |
| Electrical performance | Test Condition | Test Method | YANTAI WANHUA/CA3250 BK08011 |
|---|---|---|---|
| 10000000000000000 Q.cm | |||
| Surface Resistivity | 1000000000000000 Q |
| Flame retardant performance | Test Condition | Test Method | YANTAI WANHUA/CA3250 BK08011 |
|---|---|---|---|
| Fire rating 3.0mm | V-0 | ||
| Fire rating 1.5mm | V-0 |
| physical property | Test Condition | Test Method | YANTAI WANHUA/CA3250 BK08011 |
|---|---|---|---|
| Specific gravity 23 ℃ | 1.18 g/cm³ | ||
| 17 g/10min | |||
| Shrinkage rate flow 2.0mm | 0.5-0.7 % |
| Thermal performance | Test Condition | Test Method | YANTAI WANHUA/CA3250 BK08011 |
|---|---|---|---|
| Hot deformation temperature 1.8MPa120 ℃/hr | 82 °C | ||
| Vicat softening temperature 120 ℃/hr 50N | 102 °C |