SMA XIRAN® SE700
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | 内部方法 | 0.50 % | |
| 内部方法 | 0.20 % | ||
| Water absorption rate | ASTMD570 | 0.20 % | |
| density | ISO1183 | 1.05 g/cm³ | |
| melt mass-flow rate | ISO1133 | 22 g/10min | |
| SpiralFlow | 内部方法 | 36.0 cm |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flexural modulus | ISO178 | 8500 MPa | |
| Bending stress | ISO178 | 150 MPa | |
| Tensile modulus | ISO527-2 | 2100 MPa | |
| Tensile stress | Yield | ISO527-2 | 36.0 MPa |
| Break | ISO527-2 | 35.0 MPa | |
| Tensile strain | Break | ISO527-2 | 3.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO179/1eA | 5.0 kJ/m² | |
| ISO179/1eA | 9.0 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO179/1eU | 30 kJ/m² | |
| ISO179/1eU | 30 kJ/m² | ||
| Impact strength of cantilever beam gap | ISO180/A | 5.0 kJ/m² | |
| ISO180/A | 9.0 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear thermal expansion coefficient | ASTMD696 | 2.9E-05 cm/cm/°C | |
| ASTMD696 | 4.7E-05 cm/cm/°C | ||
| Heat Deflection Temperature | ISO75-2/A | 92.0 °C | |
| vicat | ISO306/B | 115 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.